PPS Torelina® A390M65 TORAY JAPAN

133

Unit Price:
$4593 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
54.7MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High temperature resistan Glass fiber reinforced
Application Areas:Electrical applications sporting goods Lighting fixtures
Color:--
Grade:Injection grade

Technical Data Sheet Compare

Physical properties	Test Condition	Test Method	Test Result	Unit
density		ASTM D792/ISO 1183	1.99
Water absorption rate 23 ℃/24h		ASTM D570/ISO 62	0.02	%

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD:3.00mm2	内部方法	0.50	%
Shrinkage rate	Shrinkage rate	MD:3.00mm4	内部方法	0.25	%
Water absorption rate	23°C,24hr	ISO62	0.020	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile stress	Yield,23°C	ISO527-2	105	Mpa
Tensile strain	Break,23°C	ISO527-2	0.90	%
Bending modulus	23°C	ISO178	19500	Mpa
Bending stress	23°C	ISO178	210	Mpa
shear strength	23°C	JISK7214	60.0	Mpa
Friction coefficient 4			0.30
Taber abraser	1000Cycles	ISO9352	70.0	mg
elongation at break		ASTM D638/ISO 527	0.9	%
tensile strength		ASTM D638/ISO 527	105	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	19.5	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	210	kg/cm²(MPa)[Lb/in²]
Charpy impact strength		ASTM D256/ISO 179	7	kg·cm/cm(J/M)ft·lb/in
Charpy impact strength	Charpy impact strength		ASTM D256/ISO 179	17	kg·cm/cm(J/M)ft·lb/in

Thermal performance	Test Condition	Test Method	Test Result	Unit
Combustibility (rate)		UL94	V-0
Hot deformation temperature		ASTM D648/ISO 75	>260	℃（℉）
melting point			278	℃（℉）
Linear expansion coefficient		ASTM D696/ISO 11359	1.9	mm/mm.℃
Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	260	°C
Melting temperature		ISO11357-3	278	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	1.9E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO11359-2	2.5E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity		IEC60093	1E+16	ohms·cm
Dielectric strength		IEC60243-1	21	KV/mm
Dielectric constant 6	23°C,1MHz	IEC60250	5.30
Dissipation factor 5	23°C,1MHz	IEC60250	2E-03
Volume resistivity		ASTM D257/IEC 60093	1014	Ω.cm

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	23°C	ISO179	17	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale	ISO2039-2	122

flammability	Test Condition	Test Method	Test Result	Unit
FlameRating	0.72mm	UL94	V-0

Supplementary Information	Test Condition	Test Method	Test Result	Unit
BarFlowLength6	320°C,1.00mm	内部方法	8.00	CM

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.