Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | 23°C,24hr | ISO62 | >0.020 | % |
| Density/specific gravity | | ISO1183 | 1.93 | g/cm³ |
| Shrinkage rate 1 | TD | ISO294-4 | 0.40 | % |
| Shrinkage rate 1 | MD | ISO294-4 | 0.30 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending stress | | ISO178 | 170 | Mpa |
| Tensile stress | | ISO527-2 | 114 | Mpa |
| Tensile strain | Break | ISO527-2 | 0.80 | % |
| Bending modulus | | ISO178 | 18700 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 275 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.4E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO11359-2 | 2.4E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric strength | 3.00mm | IEC60243-1 | 13 | KV/mm |
| Dielectric constant | | IEC60250 | 4.70 | |
| Volume resistivity | | ASTMD257 | 1E+16 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 7.7 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M-Sale | ISO2039-2 | 97 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5mm | UL94 | V-0 | |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| Flowability2 | 1.00mm | 内部方法 | 8.20 | CM |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.