PPS PPS-hGR30 SICHUAN DEYANG
130
- Unit Price:
- $4527 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 16MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance
- Application Areas:Electrical field Electrical appliances Electronic field Aerospace Mechanical components
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.55 |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | GB/T 15585-1995 | 0.0025 | mm/mm |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| compressive strength | GB/T 1041-1992 | 140 | Mpa | |
| Rockwell hardness | GB/T 9342-1988 | 100 | hr | |
| elongation | Break | GB/T 1040-1992 | 1.70 | % |
| Bending modulus | GB/T 1042-1992 | 1.1×104 | Mpa | |
| bending strength | GB/T 1042-1992 | 180 | Mpa | |
| Impact strength of cantilever beam gap | GB/T 1843-1996 | 11.5 | kJ/m² | |
| tensile strength | GB/T 1040-1992 | 142 | Mpa | |
| elongation at break | ASTM D638/ISO 527 | 1.7 | % | |
| tensile strength | ASTM D638/ISO 527 | 142 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 100 | ||
| Bending modulus | ASTM D790/ISO 178 | 1.1*100000 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 180 | kg/cm²(MPa)[Lb/in²] |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| melting point | 282 | ℃（℉） | ||
| GB/T 4608-1984 | 282 | °C | ||
| Hot deformation temperature | 1.80MPa | GB/T 1634-1979(1989) | 267 | °C |
| Combustibility | 垂直法 | GB/T 2408-1996 | FV-0 | 级 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric constant | 1MHz | GB/T 1409-1988 | 4 | |
| Electrical strength | GB/T 1408.1-1999 | 18.56 | KV/mm | |
| Surface resistivity | GB/T 1410-1989 | 2.3×1015 | Ω | |
| Volume resistivity | GB/T 1410-1989 | 1.0×1015 | Ω.m |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | GB/T 1033-1986 | 1.55 | g/cm³ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.