LCP SUMIKASUPER® E6008LMR B SUMITOMO JAPAN
235
Unit Price:$7873 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 70MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:dimensional stability Low warpage Low viscosity High rigidity Good forming performance Weldable Aging resistance Good adhesion Chemical resistance heat-resisting Glass fiber reinforced high strength
- Application Areas:Electrical appliances Automotive sector Electronic field Engineering accessories Food containers Household appliances Household appliances Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Across Flow | 内部方法 | 1.2 | % |
| 流量 | 内部方法 | 0.18 | % | |
| Water absorption rate | Saturation | ASTM D570 | 0.020 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTM D785 | 103 | |
| Tensile strength | ASTM D638 | 147 | Mpa | |
| elongation | Break | ASTM D638 | 5.2 | % |
| Bending modulus | 23°C | ASTM D790 | 12300 | Mpa |
| 200°C | ASTM D790 | 4900 | Mpa | |
| bending strength | 23°C | ASTM D790 | 143 | Mpa |
| 200°C | ASTM D790 | 33.0 | Mpa | |
| shear strength | ASTM D732 | 51.0 | Mpa | |
| Poisson's ratio | ASTM D785 | 0.46 | ||
| Non notched cantilever beam impact | 6.40 mm | ASTM D256 | 410 | J/m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal deformation temperature under load | 1.8 MPa, Unannealed | ASTM D648 | 279 | °C |
| Linear coefficient of thermal expansion | Flow : 150°C | 内部方法 | 1.3E-5 | cm/cm/°C |
| Across Flow : 150°C | 内部方法 | 5.6E-5 | cm/cm/°C | |
| thermal conductivity | JIS R2618 | 0.52 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | ASTM D257 | 1.0E+15 | ohms·cm | |
| Dielectric constant | 1 kHz | ASTM D150 | 4.40 | |
| 1 MHz | ASTM D150 | 3.90 | ||
| Dissipation factor | 1 kHz | ASTM D150 | 0.022 | |
| 1 MHz | ASTM D150 | 0.022 | ||
| Arc resistance | ASTM D495 | 130 | sec | |
| Leakage Trace Index | IEC 60112 | 125 | V |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 130 | °C | ||
| drying time | 4.0 到 24 | hr | ||
| Temperature at the rear of the barrel | 280 到 320 | °C | ||
| Temperature in the middle of the barrel | 320 到 350 | °C | ||
| Temperature at the front of the material cylinder | 340 到 370 | °C | ||
| Spray nozzle temperature | 340 到 370 | °C | ||
| Processing (melt) temperature | 360 | °C | ||
| Mold temperature | 40 到 160 | °C | ||
| Injection pressure | 80.0 到 160 | Mpa | ||
| Injection speed | 中等偏快 | |||
| Maintain pressure | 20.0 到 40.0 | Mpa | ||
| Back pressure | 1.00 到 5.00 | Mpa | ||
| Screw speed | 50 到 100 | rpm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.30 mm, ALL | UL 94 | V-0 | |
| Extreme Oxygen Index | ISO 527-1,-2(JIS K7161,7162) | 48 | % | |
| Soldering Resistance | 内部方法 | 300 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.