LCP ZENITE® 6130L-WT010 DUPONT USA
120
- Unit Price:
- $8803 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 23MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Filler: Glass fiber reinf 30% Filler by weight
- Application Areas:Electrical field Electronic field Aerospace Aerospace Applications Household appliances Automotive sector Application in the automo Communication equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1680 | ||
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.002 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2/1A/1 | 13000 | Mpa | |
| Tensile stress | Break | ISO527-2/1A/5 | 130 | Mpa |
| Tensile strain | Break | ISO527-2/1A/5 | 1.8 | % |
| Bending modulus | 23°C | ISO178 | 12000 | Mpa |
| Tensile modulus | ASTM D638/ISO 527 | 13500 | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 165 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 195 | kg/cm²(MPa)[Lb/in²] | |
| IZOD notch impact strength | ASTM D256/ISO 179 | 25 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 20 | kg·cm/cm(J/M)ft·lb/in | ||
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 2.7 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | ASTM D648/ISO 75 | 268 | ℃（℉） | |
| melting point | 335 | ℃（℉） | ||
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 265 | °C |
| Melting temperature 2 | ISO11357-3 | 335 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 3E-06 | cm/cm/°C |
| TD | ISO11359-2 | 7E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+16 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+16 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 36 | KV/mm | |
| Relative permittivity | 1MHz | IEC60250 | 4.00 | |
| 2.05GHz | 内部方法 | 4.16 | ||
| Dissipation factor | 1MHz | IEC60250 | 0.031 | |
| 2.05GHz | 内部方法 | 5E-03 | ||
| Leakage Trace Index | IEC60112 | 200 | V | |
| Surface resistivity | ASTM D257/IEC 60093 | 1.00E+16 | Ω | |
| Volume resistivity | ASTM D257/IEC 60093 | 1.00E+17 | Ω.cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 35 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-0 | |
| 0.38mm | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.