LCP SUMIKASUPER® E6810（BK） SUMITOMO JAPAN

143

Unit Price:
$6222 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Dimensional stability Low warpage Low viscosity High elasticity High temperature strength Aging resistance
Application Areas:Electrical field Electrical appliances Electronic field Engineering accessories Automotive sector Food containers
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	Flow	ASTM D955	0.22	%
Shrinkage rate	Shrinkage rate	Across Flow	ASTM D955	0.66	%
Water absorption rate	Saturation	ASTM D570	0.020	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile strength		ASTM D638	126	Mpa
elongation	Break	ASTM D638	4.3	%
Bending modulus	23°C	ASTM D790	13500	Mpa
bending strength	23°C	ASTM D790	134	Mpa
shear strength		ASTM D732	50.0	Mpa
Poisson's ratio		ASTM E132	0.39

Thermal performance	Test Condition	Test Method	Test Result	Unit
Thermal deformation temperature under load	1.8 MPa, Unannealed	ASTM D648	284	°C
Linear coefficient of thermal expansion	Flow : 50 to 150°C	ASTM D696	1.1E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 50 to 150°C	ASTM D696	6.5E-5	cm/cm/°C
RTI Elec	3.2 mm	UL 746	220	°C
RTI Imp	3.2 mm	UL 746	200	°C
RTI	3.2 mm	UL 746	240	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity		ASTM D257	1.0E+15	ohms·cm
Dielectric constant	1 kHz	ASTM D150	4.30
Dielectric constant	Dielectric constant	1 MHz	ASTM D150	3.90
Dissipation factor	1 kHz	ASTM D150	0.019
Dissipation factor	Dissipation factor	1 MHz	ASTM D150	0.028
Arc resistance		ASTM D495	130	sec
Compared to the Leakage Tracking Index (CTI)		UL 746	165	V

injection	Test Result	Unit
drying temperature	120 到 150	°C
drying time	3.0	hr
Suggested maximum recycled material ratio	30	%
Temperature at the rear of the barrel	300 到 320	°C
Temperature in the middle of the barrel	320 到 350	°C
Temperature at the front of the material cylinder	340 到 370	°C
Spray nozzle temperature	340 到 370	°C
Mold temperature	70 到 160	°C
Injection pressure	78.0 到 157	Mpa
Injection speed	中等偏快
Maintain pressure	20.0 到 39.0	Mpa
Back pressure	0.980 到 4.90	Mpa
Screw speed	50 到 100	rpm

Impact performance	Test Condition	Test Method	Test Result	Unit
Non notched cantilever beam impact	6.40 mm	ASTM D256	280	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale	ASTM D785	103

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.30 mm	UL 94	V-0
Extreme Oxygen Index		ASTM D2863	46	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.