LCP ZENITE® 5244L DUPONT USA
120
- Unit Price:
- $8320 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High toughness enhance Glass fiber reinforced
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ISO 1183 | 1.71 | g/cm³ | |
| Shrinkage rate | 流动 | ISO 294-4 | 0.1 | % |
| 垂直 | ISO 294-4 | 0.4 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | 断裂 | ISO 527-2/1A | 131 | Mpa |
| elongation | 断裂 | ISO 527-2/1A | 1.66 | % |
| Tensile modulus | ISO 527-2/1A | 14000 | Mpa | |
| bending strength | ISO 178 | 198 | Mpa | |
| Bending modulus | ISO 178 | 13100 | Mpa | |
| Cantilever beam without notch impact | 23.0 °C | ISO 180/1U | 28.0 | kJ/m² |
| Simple supported beam without notch impact | 23.0 °C | ISO 179/1eU | 16.6 | kJ/m² |
| Impact of simply supported beam gap | 23.0 °C | ISO 179/1eA | 27 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Coefficient of linear expansion | 流动 | ISO 11359-2 | 0.0000060 | cm/cm/°C |
| 垂直 | ISO 11359-2 | 0.000048 | cm/cm/°C | |
| Melting temperature | 10°C/min | ISO 11357-1,-2,-3 | 318 | °C |
| Hot deformation temperature | 1.8 MPa | ISO 75-1, -2 | 285 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative permittivity | 2.05 GHz | 4.18 | ||
| Dissipation factor | 2.05 GHz | 0.004 |
| Flame retardant performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Fire rating | 1.50 mm | UL94 | V-0 | |
| 0.800 mm | UL94 | V-0 |
| Processing conditions | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Mold temperature | cavity | 80.0 - 120 | °C | |
| Temperature of the cutting section | 40.0 - 60.0 | °C | ||
| The first temperature segment | 320 - 330 | °C | ||
| Second stage temperature | 335 - 345 | °C | ||
| Third stage temperature | 335 - 345 | °C | ||
| Fourth section temperature | 335 - 345 | °C | ||
| Spray nozzle temperature | 335 - 345 | °C | ||
| Processing (melt) temperature | 325 - 345 | °C | ||
| drying temperature | >= 150 | °C | ||
| drying time | 3.00 | hour | ||
| Suggested moisture content | <= 0.010 | % | ||
| Injection pressure | 50.0 - 150 | Mpa | ||
| Maintain pressure | 50.0 - 150 | Mpa | ||
| Back pressure | <= 3.00 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.