LCP VECTRA® B130 CELANESE USA
114
- Unit Price:
- $6222 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 50MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High rigidity Flame retardant enhance Glass fiber reinforced Low contractility Filler/Reinforcement Glas Packing weight of 305 Low shrinkage rate Good stiffness
- Application Areas:Home appliance components Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Mold shrinkage rate | normal | ISO 2577 | 0.0 | % |
| parallel | ISO 2577 | 0.20 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile creep modulus | 1hr | ISO 899-1 | 16000 | Mpa |
| 1000hr | ISO 899-1 | 14100 | Mpa | |
| Charpy notch impact strength | 23℃ | ISO 179/1eA | 12.0 | KJ/m |
| IZOD notch impact strength | 23℃ | ISO 180/1A | 14.0 | KJ/m |
| Tensile modulus | ISO 527-1,-2/1 | 22000 | Mpa | |
| Rockwell hardness | ISO 2039-2 | 100 | M Scale | |
| Bending modulus | 23℃ | ISO 178 | 20000 | Mpa |
| bending strength | 23℃ | ISO 178 | 300 | Mpa |
| IZOD notch free impact strength | 23℃ | ISO 180/1U | 15.0 | KJ/m |
| Fracture strain | ISO 527-1,-2/5 | 1.0 | % | |
| Fracture stress | ISO 527-1,-2/5 | 205 | Mpa | |
| Charpy impact strength | 23℃ | ISO 179/1eU | 18.0 | KJ/m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | 50℃/h 50N | ISO 306 | 169 | °C |
| Combustibility | UL 94 | V-0 | ||
| Hot deformation temperature | 0.45MPa | ISO 75-1,-2 | 250 | °C |
| 1.80MPa | ISO 75-1,-2 | 235 | °C | |
| Linear coefficient of thermal expansion | parallel | ISO 11359-1,-2 | 3E-06 | cm/cm℃ |
| normal | ISO 11359-1,-2 | 0.000013 | cm/cm℃ |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Electrical strength | IEC 60243-1 | 38 | KV/mm | |
| Dielectric loss factor | 100Hz | IEC 60250 | 0.0100 | |
| 1000Hz | IEC 60250 | 0.0080 | ||
| Surface resistivity | IEC 60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC 60093 | 1E+13 | ohm.m | |
| Relative permittivity | 100Hz | IEC 60250 | 4.00 | |
| 1000Hz | IEC 60250 | 3.50 |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Oxygen demand index | ISO 4589-1-2 | 50 | % |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | ISO 1183 | 1600 | kg/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.