LCP LAPEROS® S135 JAPAN POLYPLASTIC
120
- Unit Price:
- $6222 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 50MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced High rigidity High temperature resistan
- Application Areas:Electrical field Electronic field Engine hood parts Household appliances Household appliances Switch panel Connector Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.66 |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 0.40 | % |
| MD | ISO294-4 | 0.10 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 4E-03 | % |
| Equilibrium,23°C,50%RH | ISO62 | 7E-03 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Break | ISO527-2/1A/5 | 140 | Mpa |
| Tensile strain | Break | ISO527-2/1A/5 | 1.3 | % |
| Tensile modulus | ISO527-2/1A/1 | 15500 | Mpa | |
| tensile strength | ASTM D638/ISO 527 | 155 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 16000 | kg/cm²(MPa)[Lb/in²] | |
| 23°C | ISO178 | 14500 | Mpa | |
| bending strength | ASTM D790/ISO 178 | 220 | kg/cm²(MPa)[Lb/in²] | |
| Bending stress | 23°C | ISO178 | 230 | Mpa |
| CompressiveStress | 1%Strain | ISO604 | 114 | Mpa |
| Fracture bending strain | ISO178 | 2.0 | % | |
| Charpy impact strength | ASTM D256/ISO 179 | 12 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | ASTM D648/ISO 75 | 340 | ℃（℉） | |
| 1.8MPa,Unannealed | ISO75-2/A | 340 | °C | |
| 8.0MPa,Unannealed | ISO75-2/C | 267 | °C | |
| Melting temperature 2 | ISO11357-3 | 350 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1E-06 | cm/cm/°C |
| TD | ISO11359-2 | 2.3E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | IEC60243-1 | 37 | KV/mm | |
| Relative permittivity | 1MHz | IEC60250 | 3.50 | |
| Surface resistivity | IEC60093 | 1E+17 | ohms | |
| Arc resistance | ASTM D495/IEC 60112 | 138 | ||
| Volume resistivity | IEC60093 | 1E+17 | ohms·cm | |
| Dissipation factor | 1MHz | IEC60250 | 9E-03 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unscented Izod impact strength | 23°C | ISO180/1U | 14 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.