PC/ABS INFINO® HP-1000XA K21315 Samsung Cheil South Korea
92
- Unit Price:
- $2642 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Easy to process High impact resistance heat-resisting Thermal stability High rigidity Dimensional stability Chemical resistance
- Application Areas:Application in the automo Engineering accessories Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD:3.20mm | ISO2577 | 0.40to0.70 | % |
| Melt mass flow rate | 250°C/10.0kg | ASTMD1238 | 27 | g/10min |
| 250°C/10.0kg | ISO1133 | 27 | g/10min | |
| Shrinkage rate | MD：3.20mm | ASTMD955 | 0.40to0.70 | % |
| TD：3.20mm | ASTMD955 | 0.40to0.70 | % | |
| TD:3.20mm | ISO2577 | 0.40to0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 2 | ASTMD638 | 2000 | Mpa | |
| Tensile modulus | ISO527-2/50 | 2000 | Mpa | |
| Tensile strength 2 | Yield | ASTMD638 | 54.0 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 50.0 | Mpa |
| Tensile strength 2 | Break | ASTMD638 | 59.0 | Mpa |
| Tensile stress | Break | ISO527-2/50 | 53.0 | Mpa |
| Elongation rate 2 | Break | ASTMD638 | 100 | % |
| Tensile strain | Break | ISO527-2/50 | 100 | % |
| Bending modulus 3 | ASTMD790 | 2000 | Mpa | |
| Bending modulus 4 | ISO178 | 2100 | Mpa | |
| Bending strength 3 | ASTMD790 | 74.0 | Mpa | |
| Bending stress 4 | ISO178 | 80.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,4.00mm | ISO75-2/B | 123 | °C |
| 0.45MPa,Annealed,4.00mm | ISO75-2/B | 125 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 110 | °C | |
| 1.8MPa,Unannealed,4.00mm | ISO75-2/A | 102 | °C | |
| 1.8MPa,Annealed,4.00mm | ISO75-2/A | 112 | °C | |
| Vicat softening temperature | -- | ISO306/B50 | 123 | °C |
| -- | ISO306/B120 | 125 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| CharpyNotchedImpactStrength5 | 23°C | ISO179/1eA | 49 | kJ/m² |
| Suspended wall beam gap impact strength 5 | 23°C | ISO180/1A | 45 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTMD785 | 113 | |
| R-Scale | ISO2039-2 | 113 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.