PC/ABS CYCOLOY™ CX7240-7T2A6747 SABIC INNOVATIVE SHANGHAI

102

Unit Price:
$3188 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant High impact resistance High mobility
Application Areas:Electrical field Electronic field Engine hood parts Medical supplies Electronic display Aerospace Applications Nursing supplies Architectural application Outdoor applications Liquid handling Lighting fixtures
Color:--
Grade:High liquidity level

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Melt flow rate	260°C/2.16 kg	ASTM D1238	18	g/10 min
Molten Volume Flow Rate (MVR)	260°C/2.16 kg	ISO 1133	15.0	cm3/10min
Shrinkage rate - flow	3.20 mm	内部方法	0.40 到 0.60	%
Water absorption rate	Saturation, 23°C	ISO 62	0.20	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.10	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	-- 2	ASTM D638	2600	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2600	Mpa
Tensile strength	Yield 3	ASTM D638	65.0	Mpa
	Tensile strength	Yield	ISO 527-2/50	65.0	Mpa
		Tensile strength	Break 3	ASTM D638	58.0	Mpa
		Tensile strength	Tensile strength	Break	ISO 527-2/50	50.0	Mpa
elongation	Yield 3	ASTM D638	4.1	%
	elongation	Yield	ISO 527-2/50	4.0	%
		elongation	Break 3	ASTM D638	100	%
		elongation	elongation	Break	ISO 527-2/50	90	%
Bending modulus	50.0 mm Span 4	ASTM D790	2500	Mpa
Bending modulus	Bending modulus	-- 5	ISO 178	2500	Mpa
Bending stress	-- 5, 6	ISO 178	96.0	Mpa
Bending stress	Bending stress	Yield, 50.0 mm Span 4	ASTM D790	104	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Thermal deformation temperature under load	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	100	°C
	Thermal deformation temperature under load	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	89.0	°C
		Thermal deformation temperature under load	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	99.0	°C
		Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 10	ISO 75-2/Af	93.0	°C
Vicat softening temperature	--	ASTM D152511, ISO 306/B5011	110	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	113	°C
Ball Pressure Test	73 to 77°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831, ISO 11359-2	7.5E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.5E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	7.5E-5	cm/cm/°C
thermal conductivity		ISO 8302	0.20	W/m/K
RTI Elec		UL 746	90.0	°C
RTI Imp		UL 746	90.0	°C
RTI		UL 746	90.0	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC 60093	> 1.0E+15	ohms
Volume resistivity		IEC 60093	> 1.0E+15	ohms·cm
Dielectric strength	0.800 mm, in Oil	IEC 60243-1	35	KV/mm
	Dielectric strength	1.60 mm, in Oil	IEC 60243-1	25	KV/mm
	Dielectric strength	Dielectric strength	3.20 mm, in Oil	IEC 60243-1	17	KV/mm
Compared to the Leakage Tracking Index (CTI)		UL 746	PLC 3
High arc combustion index (HAI) 12		UL 746	PLC 0
Hot wire ignition (HWI)		UL 746	PLC 3

injection	Test Result	Unit
drying temperature	80 到 90	°C
drying time	2.0 到 4.0	hr
Suggested maximum moisture content	0.020	%
Hopper temperature	60 到 80	°C
Temperature at the rear of the barrel	230 到 280	°C
Temperature in the middle of the barrel	240 到 290	°C
Temperature at the front of the material cylinder	250 到 300	°C
Spray nozzle temperature	250 到 300	°C
Processing (melt) temperature	250 到 300	°C
Mold temperature	60 到 85	°C
Exhaust hole depth	0.030 到 0.075	mm

Impact performance	Test Condition	Test Method	Test Result	Unit
Dart impact equipped with measuring instruments	23°C, Total Energy	ASTM D3763	65.0	J

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.60 mm	UL 94	V-1
	UL flame retardant rating	0.75 mm	UL 94	V-0
		UL flame retardant rating	1.5 mm	UL 94	5VB
		UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA
Burning wire flammability index	0.75 mm	IEC 60695-2-12	960	°C
Burning wire flammability index	Burning wire flammability index	0.75 mm 13	IEC 60695-2-12	960	°C
Hot filament ignition temperature	0.75 mm 13	IEC 60695-2-13	775	°C
	Hot filament ignition temperature	1.0 mm	IEC 60695-2-13	825	°C
		Hot filament ignition temperature	1.5 mm 13	IEC 60695-2-13	775	°C
			Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	800	°C
			Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm 13	IEC 60695-2-13	775	°C
Extreme Oxygen Index		ISO 4589-2	34	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.