PC/ABS Bayblend® FR3013 901510 COVESTRO THAILAND
144
Unit Price:$2995 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Impact modification
- Application Areas:Household appliances Electronic field Electrical field
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Molten Volume Flow Rate (MVR) | 240°C/5.0 kg | ISO 1133 | 26.0 | cm3/10min |
| Shrinkage rate - lateral flow rate | 2.00 mm 3 | ISO 294-4 | 0.40 到 0.60 | % |
| 3.00 mm 4 | ISO 2577 | 0.40 到 0.60 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2/1 | 2650 | Mpa |
| Tensile stress | Yield, 23°C | ISO 527-2/50 | 61.0 | Mpa |
| Break, 23°C | ISO 527-2/50 | 44.0 | Mpa | |
| Tensile strain | Yield, 23°C | ISO 527-2/50 | 4.0 | % |
| Break, 23°C | ISO 527-2/50 | 30 | % | |
| Unscented Izod impact strength | 23°C | ISO 180 | 无断裂 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 86.0 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 78.0 | °C | |
| Vicat softening temperature | -- | ISO 306/B50 | 89.0 | °C |
| -- | ISO 306/B120 | 95.0 | °C | |
| Linear coefficient of thermal expansion | Flow : 23 to 55°C | ISO 11359-2 | 7.5E-5 | cm/cm/°C |
| Across Flow : 23 to 55°C | ISO 11359-2 | 7.6E-5 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | 5.0E+17 | ohms | |
| Volume resistivity | 23°C | IEC 60093 | 2.0E+18 | ohms·cm |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Viscosity | 240°C | ISO 11443-A | 155 | Pa·s |
| ISO | PC+ABS-FR(40) |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80 | °C | ||
| Drying time - Dry Air Dryer | 4.0 | hr | ||
| Suggested maximum moisture content | < 0.020 | % | ||
| Suggested injection volume | 30 到 70 | % | ||
| Temperature at the rear of the barrel | 220 到 230 | °C | ||
| Temperature in the middle of the barrel | 225 到 235 | °C | ||
| Temperature at the front of the material cylinder | 230 到 240 | °C | ||
| Spray nozzle temperature | 255 到 265 | °C | ||
| Processing (melt) temperature | 240 到 270 | °C | ||
| Mold temperature | 60 到 90 | °C | ||
| Back pressure | 5.00 到 15.0 | Mpa | ||
| Exhaust hole depth | 0.025 到 0.075 | mm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 5VB | |
| Extreme Oxygen Index | ISO 4589-2 | 31 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.