PC/ABS CYCOLOY™ CX7240U 7M1D051 SABIC INNOVATIVE NANSHA

155

Unit Price:$4336 USD/MT

Packaging Specification:: 25 KG/PKG

Supply Quantity:: 76.1MT

Delivery Terms:: FOB

Port of Loading:: China Main Port

Accepted Payment Methods:: T/T

Shipping:: Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant High impact resistance High mobility
Application Areas:Electrical field Electronic field Architectural application Outdoor applications Engine hood parts Medical supplies Nursing supplies Plastic bag Casters Aerospace Applications Liquid handling
Color:--
Grade:Injection grade

Technical Data Sheet Compare

Physical	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate	260°C/2.16 kg	ASTM D1238	16	g/10 min
Melt Volume flow Rate	260°C/2.16 kg	ISO 1133	15.0	cm3/10min
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.40 到 0.60	%
Moisture Absorption	饱和, 23°C	ISO 62	0.20	%
Moisture Absorption	Moisture Absorption	平衡, 23°C, 50% RH	ISO 62	0.10	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45 MPa, 未退火, 3.20 mm	ASTM D648	100	°C
	Deflection Temperature Under Load?	1.8 MPa, 未退火, 3.20 mm	ASTM D648	89.0	°C
		Deflection Temperature Under Load?	1.8 MPa, 未退火, 6.40 mm	ASTM D648	99.0	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9	ISO 75-2/Af	93.0	°C
Vicat Softening Temperature	--	ASTM D152510	106	°C
	Vicat Softening Temperature	--	ISO 306/B50	110	°C
	Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	113	°C
Ball PressureTest	73 到 77°C	IEC 60695-10-2	通过
Linear thermal expansion coefficient	流动 : -40 到 40°C	ASTM E831	6.3E-5	cm/cm/°C
	Linear thermal expansion coefficient	流动 : -40 到 40°C	ISO 11359-2	6.2E-5	cm/cm/°C
		Linear thermal expansion coefficient	横向 : -40 到 40°C	ASTM E831	5.4E-5	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	横向 : -40°C	ISO 11359-2	5.4E-5	cm/cm/°C
RTI Elec		UL 746	90.0	°C
RTI Imp		UL 746	90.0	°C
RTI		UL 746	90.0	°C

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.40 mm	UL 94	V-2
	UL flame retardant rating	0.60 mm	UL 94	V-1
		UL flame retardant rating	0.75 mm	UL 94	V-0
			UL flame retardant rating	1.5 mm	UL 94	5VB
			UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA
Glow Wire Flammability Index	0.75 mm	IEC 60695-2-12	960	°C
Glow Wire Ignition Temperature	1.0 mm	IEC 60695-2-13	825	°C
Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.0 mm	IEC 60695-2-13	800	°C

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Modulus	-- 2	ASTM D638	2950	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	2530	Mpa
Tensile Strength	屈服	ISO 527-2/50	65.0	Mpa
	Tensile Strength	断裂 3	ASTM D638	58.0	Mpa
		Tensile Strength	屈服 3	ASTM D638	65.0	Mpa
		Tensile Strength	Tensile Strength	断裂	ISO 527-2/50	50.0	Mpa
Tensile Elongation	屈服 3	ASTM D638	4.1	%
	Tensile Elongation	屈服	ISO 527-2/50	4.0	%
		Tensile Elongation	断裂 3	ASTM D638	100	%
		Tensile Elongation	Tensile Elongation	断裂	ISO 527-2/50	90	%
Flexural Modulus	50.0 mm 跨距 4	ASTM D790	2750	Mpa
Flexural Modulus	Flexural Modulus	-- 5	ISO 178	2500	Mpa
Flexural Stress	-- 5, 6	ISO 178	96.0	Mpa
Flexural Stress	Flexural Stress	屈服, 50.0 mm 跨距 4	ASTM D790	104	Mpa

Electrical Properties	Test Method	Test Result
Comparative Tracking Index	UL 746	PLC 3
High Amp Arc Ignition	UL 746	PLC 0
Hot-wire Ignition	UL 746	PLC 3

Injection	Test Result	Unit
Drying Temperature	90	°C
Drying Time	4.0	hr
Suggested Max Moisture	0.040	%
Suggested Shot Size	40 到 80	%
Hopper Temperature	60 到 80	°C
Rear Temperature	260 到 300	°C
Middle Temperature	260 到 300	°C
Front Temperature	265 到 300	°C
Nozzle Temperature	265 到 300	°C
Processing (Melt) Temp	270 到 300	°C
Mold Temperature	60 到 90	°C
Vent Depth	0.038 到 0.076	mm
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	20	kJ/m²
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	65.0	J

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.