PC/ABS LUPOY® HR-5007AE LG GUANGZHOU
110
- Unit Price:
- $3891 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 51MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:heat-resisting
- Application Areas:Electrical applications Electrical components Automotive interior parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm,InjectionMolded | ASTMD955 | 0.50to0.80 | % |
| Water absorption rate | Saturation | ISO622 | 0.15 | % |
| Melt mass flow rate | 250°C/2.16kg | ASTMD1238 | 5.3 | g/10min |
| Melt volume flow rate | 260°C/5.0kg | ASTMD1505 | 18.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending modulus 4 | 3.20mm,InjectionMolded | ASTMD790 | 2110 | Mpa |
| Bending strength 4 | 3.20mm | ASTMD790 | 77.5 | Mpa |
| Tensile strength 2 | Yield,3.20mm,Injection | ASTMD638 | 56.9 | Mpa |
| Tensile strain 3 | Break,3.20mm,InjectionMolded | ASTMD638 | >100 | % |
| Nominal strainatbreak | ISO527-22 | >50 | % | |
| Tensile modulus | ISO527-22 | 2200 | Mpa | |
| Tensile stress | Yield | ISO527-22 | 60.0 | Mpa |
| Tensile strain | Yield | ISO527-22 | 4.9 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTIElec | 3.0mm | UL746 | 60.0 | °C |
| 1.6mm | UL746 | 60.0 | °C | |
| Evolution Calendar intelligent importer | 3.0mm | UL746 | 60.0 | °C |
| 1.6mm | UL746 | 60.0 | °C | |
| RTIStr | 1.6mm | UL746 | 60.0 | °C |
| 3.0mm | UL746 | 60.0 | °C | |
| Hot deformation temperature | 1.8MPa | ISO75-22 | 104 | °C |
| 1.8MPa,Unannealed,6.40mm,InjectionMolded | ASTMD648 | 113 | °C | |
| Linear coefficient of thermal expansion | TD | ISO11359-22 | 8.3E-05 | cm/cm/°C |
| MD | ISO11359-22 | 7.7E-05 | cm/cm/°C | |
| Vicat softening temperature | 50N | ISO3062 | 119 | °C |
| Glass transition temperature 9 | ISO11357-22 | 150 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| High voltage arc ignition resistance index | PLC | UL746 | PLC6 | |
| Electrical strength | IEC60243-12 | 42 | KV/mm | |
| Compared to the anti leakage trace index | CTI | UL746 | PLC0 | |
| Compared to the leakage trace index | ISO 2577 | 200 | ||
| High arc combustion index (HAI) | 3.0mm | UL746 | PLC1 | |
| 1.6mm | UL746 | PLC1 | ||
| Hot wire ignition (HWI) | 1.6mm | UL746 | PLC3 | |
| 3.0mm | UL746 | PLC3 | ||
| Relative permittivity | 1MHz | ASTM D1646 | 2.80 | |
| Surface resistivity | IEC600932 | 3.8E+14 | ohms | |
| Arc resistance | ASTMD495 | PLC6 | ||
| Volume resistivity | IEC600932 | >1.0E+13 | ohms·m | |
| Dissipation factor | 1MHz | ASTM D1646 | 0.010 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpynotchedimimpact string | 23°C | ISO179/1eA2 | NoBreak | |
| Charpy impact strength | 23°C | ISO179/1eU2 | NoBreak | |
| Charpyimpactstrength | -30°C | ISO179/1eU2 | NoBreak |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTMD785 | 114 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL94 | HB | |
| 3.0mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.