PC/ABS CYCOLAC™ C7230P 5MD018 SABIC INNOVATIVE US

100

Unit Price:
$4019 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
15MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Aging resistance High mobility
Application Areas:Electronic and electrical Household appliances Lighting fixtures
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Melt flow rate		ASTM D1238	13
Melt flow rate	Melt flow rate		ASTM D1238	@Load 2.16 kg, Temperature 260
Water absorption		23°C / 50% RH; ISO 62	0.04	%
Saturated water absorption rate		ISO 62	0.09	%
Linear molding shrinkage rate, Flow		SABIC method	0.0025 - 0.0035	cm/cm
Compound melt index		MVR [cm^3/10 min]; ISO 1133	49.0 µm/m-°C	g/10 min
Compound melt index	Compound melt index			@Load 2.16 kg, Temperature 260

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Elongation (fracture)		ISO 178	30	%
Elongation (fracture)	Elongation (fracture)		Type I, 50 mm/min; ASTM D638	32	%
elongation at yield		ISO 178	3.8	%
elongation at yield	elongation at yield		Type I, 50 mm/min; ASTM D638	4	%
Tensile strength (yield)		ISO 178	35	Mpa
	Tensile strength (yield)		Type I, 50 mm/min; ASTM D638	45	Mpa
		Tensile strength (yield)		ISO 178	55	Mpa
		Tensile strength (yield)	Tensile strength (yield)		Type I, 50 mm/min; ASTM D638	58	Mpa
Tensile modulus		GB/T 15585-1995	5.2
Tensile modulus	Tensile modulus		1 mm/min; ISO 527	5.58
Bending modulus		1.3 mm/min, 50 mm span; ASTM D790	4.53
Bending modulus	Bending modulus		2 mm/min; ISO 178	4.58
bending strength		1.3 mm/min, 50 mm span; ASTM D790	98	Mpa
bending strength	bending strength		2 mm/min; ISO 178	99	Mpa
Charpy Notched Impact Strength		Edgew 80104 sp=62mm; ISO 179/1eA	0.5	J/cm²
Impact strength of cantilever beam gap		ASTM D256	0.69	J/cm
	Impact strength of cantilever beam gap		ASTM D256	0.55	J/cm
		Impact strength of cantilever beam gap			@Temperature -30.0
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		80104; ISO 180/1A	5	kJ/m²

Thermal performance	Test Condition	Test Method	Test Result	Unit
Vicat softening temperature		Rate B/50; ISO 306	107
	Vicat softening temperature		Rate B/50; ASTM D1525	108
	Vicat softening temperature	Vicat softening temperature		Equate	110
Linear coefficient of thermal expansion - flow		GB 1040	42	µm/m-°C
	Linear coefficient of thermal expansion - flow		GB 1040
		Linear coefficient of thermal expansion - flow		ISO 11359-2	42	µm/m-°C
		Linear coefficient of thermal expansion - flow	Linear coefficient of thermal expansion - flow		ISO 11359-2
Linear coefficient of thermal expansion, lateral flow		GB 1040	49	µm/m-°C
	Linear coefficient of thermal expansion, lateral flow		GB 1040
		Linear coefficient of thermal expansion, lateral flow		ISO 11359-2	59	µm/m-°C
		Linear coefficient of thermal expansion, lateral flow	Linear coefficient of thermal expansion, lateral flow		ISO 11359-2
Thermal deformation temperature under load (1.8 MPa)		Flatw 80104 sp=64mm; ISO 75/Af	89
	Thermal deformation temperature under load (1.8 MPa)		ASTMF1249	88
	Thermal deformation temperature under load (1.8 MPa)	Thermal deformation temperature under load (1.8 MPa)
Flammability (UL94)		UL 94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.