| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | Across Flow | ISO 2577 | 0.40 到 0.60 | % |
| Shrinkage rate | 流量 | ISO 2577 | 0.40 到 0.60 | % |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.40 | % |
| Water absorption rate | Equilibrium, 23°C, 50% RH | ISO 62 | 0.10 | % |
| Molten Volume Flow Rate (MVR) | 240°C/5.0 kg | ISO 1133 | 20.0 | cm3/10min |
| density | 23°C | ISO 1183 | 1.18 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | Yield, 23°C | ISO 527-2/50 | 64.0 | Mpa |
| Tensile strain | Yield, 23°C | ISO 527-2/50 | 3.9 | % |
| Tensile modulus | 23°C | ISO 527-2/1 | 2650 | Mpa |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | 40 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 95.0 | °C |
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 85.0 | °C |
| Vicat softening temperature | | ISO 306/B120 | 103 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC 60093 | 1.0E+16 | ohms |
| Volume resistivity | 23°C | IEC 60093 | 1.0E+16 | ohms·cm |
| Relative permittivity | 23°C, 100 Hz | IEC 60250 | 3.00 | |
| Relative permittivity | 23°C, 1 MHz | IEC 60250 | 2.90 | |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Viscosity | 240°C | ISO 11443-A | 150 | Pa·s |
| ISO 9660 | | | PC+ABS-FR(40) | |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying Temperature - Dry Air Dryer | | | 80 | °C |
| Drying time - Dry Air Dryer | | | 4.0 | hr |
| Suggested injection volume | | | 30 到 70 | % |
| Temperature at the rear of the barrel | | | 220 到 230 | °C |
| Temperature in the middle of the barrel | | | 225 到 235 | °C |
| Temperature at the front of the material cylinder | | | 230 到 240 | °C |
| Spray nozzle temperature | | | 255 到 265 | °C |
| Back pressure | | | 5.00 到 15.0 | Mpa |
| Exhaust hole depth | | | 0.025 到 0.075 | mm |
| Suggested maximum moisture content | | | < 0.020 | % |
| Processing (melt) temperature | | | 240 到 270 | °C |
| Mold temperature | | | 60 到 90 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 30 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Extreme Oxygen Index 3 | | ISO 4589-2 | 34 | % |
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 | |
| UL flame retardant rating | 2.0 mm | UL 94 | 5VB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.