Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| density | 23°C | ISO 1183 | 1.18 | g/cm³ |
| Molten Volume Flow Rate (MVR) | 240°C/5.0 kg | ISO 1133 | 20.0 | cm3/10min |
| Shrinkage rate | Across Flow | ISO 2577 | 0.40 到 0.60 | % |
| Shrinkage rate | 流量 | ISO 2577 | 0.40 到 0.60 | % |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.40 | % |
| Water absorption rate | Equilibrium, 23°C, 50% RH | ISO 62 | 0.10 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | 23°C | ISO 527-2/1 | 2650 | Mpa |
| Tensile stress | Yield, 23°C | ISO 527-2/50 | 64.0 | Mpa |
| Tensile strain | Yield, 23°C | ISO 527-2/50 | 3.9 | % |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | 40 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 95.0 | °C |
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 85.0 | °C |
| Vicat softening temperature | | ISO 306/B120 | 103 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC 60093 | 1.0E+16 | ohms |
| Volume resistivity | 23°C | IEC 60093 | 1.0E+16 | ohms·cm |
| Relative permittivity | 23°C, 100 Hz | IEC 60250 | 3.00 | |
| Relative permittivity | 23°C, 1 MHz | IEC 60250 | 2.90 | |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Viscosity | 240°C | ISO 11443-A | 150 | Pa·s |
| ISO 9660 | | | PC+ABS-FR(40) | |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying Temperature - Dry Air Dryer | | | 80 | °C |
| Drying time - Dry Air Dryer | | | 4.0 | hr |
| Suggested maximum moisture content | | | < 0.020 | % |
| Suggested injection volume | | | 30 到 70 | % |
| Temperature at the rear of the barrel | | | 220 到 230 | °C |
| Temperature in the middle of the barrel | | | 225 到 235 | °C |
| Temperature at the front of the material cylinder | | | 230 到 240 | °C |
| Spray nozzle temperature | | | 255 到 265 | °C |
| Processing (melt) temperature | | | 240 到 270 | °C |
| Mold temperature | | | 60 到 90 | °C |
| Back pressure | | | 5.00 到 15.0 | Mpa |
| Exhaust hole depth | | | 0.025 到 0.075 | mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 30 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 | |
| UL flame retardant rating | 2.0 mm | UL 94 | 5VB | |
| Extreme Oxygen Index 3 | | ISO 4589-2 | 34 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.