PC/ABS CYCOLAC™ C1200HF SABIC INNOVATIVE US
116
- Unit Price:
- $2758 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 46MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance heat-resisting
- Application Areas:Electrical field Electronic field Automotive interior parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Melt mass flow rate | 260°C/5.0kg | ASTMD1238 | 19 | g/10min |
| Melt volume flow rate | 265°C/5.0kg | ISO1133 | 24.0 | cm3/10min |
| Density/specific gravity | ASTMD792 | 1.15 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending stress | ISO178 | 86.0 | Mpa | |
| Elongation rate 4 | Break | ASTMD638 | 150 | % |
| Tensile modulus | ISO527-2/1 | 2370 | Mpa | |
| Bending modulus | ISO178 | 2250 | Mpa | |
| Tensile stress | Yield | ISO527-2/50 | 55.0 | Mpa |
| Tensile strain | Yield | ISO527-2/50 | 4.8 | % |
| Break | ISO527-2/50 | 110 | % | |
| Elongation rate 3 | Yield | ASTMD638 | 5.0 | % |
| Tensile modulus 2 | ASTMD638 | 2280 | Mpa | |
| Tensile strength 3 | Yield | ASTMD638 | 57.2 | Mpa |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 2340 | Mpa |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 88.3 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTIElec | UL746 | 105 | °C | |
| Evolution Calendar intelligent importer | UL746 | 80.0 | °C | |
| RTIStr | UL746 | 105 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 7.2E-05 | cm/cm/°C |
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 129 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 113 | °C | |
| Vicat softening temperature | ISO306/B50 | 130 | °C | |
| Hot deformation temperature 6 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 130 | °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 110 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot wire ignition | HWI | UL746 | PLC3 | |
| High arc combustion index | HAI | UL746 | PLC1 | |
| Compared to the anti leakage trace index | CTI | UL746 | PLC2 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Suspended wall beam gap impact strength 5 | -30°C | ISO180/1A | 34 | kJ/m² |
| 23°C | ISO180/1A | 49 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 480 | J/m |
| 23°C | ASTMD256 | 590 | J/m | |
| Dart impact equipped with measuring instruments | -30°C,TotalEnergy | ASTMD3763 | 54.2 | J |
| 23°C,TotalEnergy | ASTMD3763 | 54.2 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 1.2mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.