PC/ABS IUPILON™ MB-1800 MITSUBISHI ENGINEERING JAPAN
130
- Unit Price:
- $3258 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility
- Application Areas:Electronic and Electrical Shell
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.18 | ||
| Molding shrinkage rate | ASTM D955 | 0.3-0.5 | % | |
| Melt index (flow coefficient) | ASTM D1238/ISO 1133 | 14 | g/10min | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.2 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 260°C/2.16kg | ISO1133 | 14 | g/10min |
| Melt volume flow rate | 260°C/2.16kg | ISO1133 | 14.0 | cm3/10min |
| Shrinkage rate | TD:3.20mm | 0.30to0.50 | % | |
| MD:3.20mm | 0.30to0.50 | % | ||
| Water absorption rate | Saturation,23°C | ISO62 | 0.20 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 2800 | Mpa | |
| Tensile stress | Yield | ISO527-2 | 60.0 | Mpa |
| Tensile strain | Yield | ISO527-2 | 4.0 | % |
| Nominal tensile fracture strain | ISO527-2 | 92 | % | |
| Bending modulus | ISO178 | 2800 | Mpa | |
| Bending stress | ISO178 | 95.0 | Mpa | |
| elongation at break | ASTM D638/ISO 527 | 92 | % | |
| Tensile modulus | ASTM D638/ISO 527 | 2800 | kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 60 | % | |
| Bending modulus | ASTM D790/ISO 178 | 2800 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 95 | kg/cm²(MPa)[Lb/in²] | |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 4.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 89.0 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 81.0 | °C | |
| Combustibility (rate) | UL94 | V-0(1.2mm) | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 81 | ℃（℉） | |
| ASTM D648/ISO 75 | 89 | ℃（℉） |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179 | NoBreak |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.2mm | UL94 | V-0 | |
| 2.0mm | UL94 | 5VB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.