PC/ABS CYCOLAC™ C1200HF-701 SABIC INNOVATIVE US
124
- Unit Price:
- $2519 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance heat-resisting
- Application Areas:Electrical field Electronic field Automotive interior parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | 260°C/5.0 kg | ASTM D1238 | 19 | g/10 min |
| Molten Volume Flow Rate (MVR) | 265°C/5.0 kg | ISO 1133 | 24.0 | cm3/10min |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | -- 2 | ASTM D638 | 2270 | Mpa |
| -- | ISO 527-2/1 | 2360 | Mpa | |
| elongation | Yield 3 | ASTM D638 | 5.0 | % |
| Yield | ISO 527-2/50 | 4.8 | % | |
| Break 3 | ASTM D638 | 150 | % | |
| Break | ISO 527-2/50 | 110 | % | |
| Bending modulus | 50.0 mm Span 4 | ASTM D790 | 2340 | Mpa |
| -- | ISO 178 | 2250 | Mpa | |
| Tensile strength | Yield 3 | ASTM D638 | 57.0 | Mpa |
| Yield | ISO 527-2/50 | 55.0 | Mpa | |
| Bending stress | -- | ISO 178 | 86.0 | Mpa |
| Yield, 50.0 mm Span 4 | ASTM D790 | 88.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTI | UL 746 | 105 | °C | |
| RTI Imp | UL 746 | 80.0 | °C | |
| RTI Elec | UL 746 | 105 | °C | |
| Vicat softening temperature | ISO 306/B50 | 130 | °C | |
| Linear coefficient of thermal expansion - flow | -40 to 40°C | ASTM E831 | 7.2E-5 | cm/cm/°C |
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 129 | °C |
| 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 6 | ISO 75-2/Bf | 130 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 112 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 6 | ISO 75-2/Af | 110 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | ||
| High arc combustion index (HAI) 7 | UL 746 | PLC 1 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 3 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hopper temperature | 60 到 80 | °C | ||
| drying time | 3.0 到 4.0 | hr | ||
| Suggested injection volume | 30 到 80 | % | ||
| Temperature at the rear of the barrel | 250 到 290 | °C | ||
| Temperature in the middle of the barrel | 255 到 295 | °C | ||
| Temperature at the front of the material cylinder | 260 到 300 | °C | ||
| Spray nozzle temperature | 275 到 300 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 40 到 70 | rpm | ||
| Exhaust hole depth | 0.038 到 0.076 | mm | ||
| drying temperature | 100 到 110 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 275 到 300 | °C | ||
| Mold temperature | 60 到 90 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | -30°C, Total Energy | ASTM D3763 | 54.0 | J |
| 23°C, Total Energy | ASTM D3763 | 54.0 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.2 mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.