PC LEXAN™ 943X-8G6A4064 SABIC INNOVATIVE NANSHA
135
Unit Price:$3239 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Easy to process Impact modification Bromine free
- Application Areas:Electrical appliances Plastic bag
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 熔体质量流动速率 | 300°C/1.2kg | ASTMD1238 | 10 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 9.00 | cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40to0.80 | % |
| TD：3.20mm | 内部方法 | 0.40to0.80 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.35 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ASTMD638 | 2100 | Mpa | |
| ISO527-2/1 | 2100 | Mpa | ||
| Tensile strength | Yield | ASTMD638 | 58.0 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 55.0 | Mpa |
| Tensile strength | Break | ASTMD638 | 60.0 | Mpa |
| Tensile stress | Break | ISO527-2/50 | 60.0 | Mpa |
| Elongation rate | Yield | ASTMD638 | 6.0 | % |
| Tensile strain | Yield | ISO527-2/50 | 6.0 | % |
| Elongation rate | Break | ASTMD638 | 130 | % |
| Tensile strain | Break | ISO527-2/50 | 130 | % |
| Bending modulus | 50.0mmSpan | ASTMD790 | 2060 | Mpa |
| ISO178 | 2200 | Mpa | ||
| Bending strength 5, | ISO178 | 85.0 | Mpa | |
| Unscented Izod Impact Strength | 23°C | ISO180/1U | NoBreak | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 50.0 | J |
| Bending strength | Yield,50.0mmSpan | ASTMD790 | 89.0 | Mpa |
| Impact strength of simply supported beam gap | -30°C | ISO179/1eA | 60 | kJ/m² |
| 23°C | ISO179/1eA | 75 | kJ/m² | |
| The impact strength of a simply supported beam without a notch is | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Suspended wall beam gap impact strength | -30°C | ISO180/1A | 50 | kJ/m² |
| 23°C | ISO180/1A | 70 | kJ/m² | |
| Unscented Izod Impact Strength | -30°C | ISO180/1U | NoBreak |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 135 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 120 | °C | |
| Vicat softening temperature | ASTMD15259 | 140 | °C | |
| ISO306/B120 | 140 | °C | ||
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 6.5E-05 | cm/cm/°C |
| MD：23to80°C | ISO11359-2 | 7.2E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 6.5E-05 | cm/cm/°C | |
| TD：23to80°C | ISO11359-2 | 7.7E-05 | cm/cm/°C | |
| RTIElec | UL746 | 125 | °C | |
| Evolution Calendar intelligent importer | UL746 | 115 | °C | |
| RTIStr | UL746 | 120 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 3.20mm,inOil | ASTMD149 | 17 | KV/mm |
| 3.20mm,in Oil | IEC60243-1 | 16 | KV/mm | |
| Dielectric constant | 50Hz | ASTMD150 | 2.95 | |
| 60Hz | ASTMD150 | 2.95 | ||
| 1MHz | ASTMD150 | 2.90 | ||
| Dissipation factor | 50Hz | ASTMD150 | 2.4E-03 | |
| 60Hz | ASTMD150 | 2.4E-03 | ||
| 1MHz | ASTMD150 | 8.5E-03 | ||
| Compared to the anti leakage trace index | CTI | UL746 | PLC3 | |
| Leakage Trace Index | IEC60112 | 225 | V | |
| High arc combustion index | HAI | UL746 | PLC0 | |
| Hot wire ignition | HWI | UL746 | PLC1 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-0 | |
| 3.0mm | UL94 | 5VA | ||
| Burning wire flammability index | 1.0mm | IEC60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 1.0mm | IEC60695-2-13 | 825 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.