PC LEXAN™ HP2-8H9D375 SABIC INNOVATIVE US

Unit Price:
$4932 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
15MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High mobility
Application Areas:medicine medical care
Color:--
Grade:Medical grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	MD：3.20mm	内部方法	0.50to0.70	%
Water absorption rate	24hr	ASTMD570	0.15	%
	Water absorption rate	Equilibrium,23°C	ASTMD570	0.35	%
	Water absorption rate	Water absorption rate	Equilibrium,100°C	ASTMD570	0.58	%
Melt mass flow rate	300°C/1.2kg	ASTMD1238	18	g/10min
Melt volume flow rate	300°C/1.2kg	ISO1133	16.0	cm3/10min
Specific volume		ASTMD792	0.830	cm³/g

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Bending modulus 5		ISO178	2300	Mpa
Elongation rate 4	Break	ASTMD638	130	%
Bending strength 5,6		ISO178	90.0	Mpa
Elongation rate 3	Yield	ASTMD638	7.0	%
Tensile modulus 2		ASTMD638	2370	Mpa
Tensile strength 3	Break	ASTMD638	68.0	Mpa
Tensile strength 3	Tensile strength 3	Yield	ASTMD638	62.0	Mpa
Bending modulus 4	50.0mmSpan	ASTMD790	2340	Mpa
Bending strength 4	Yield,50.0mmSpan	ASTMD790	96.0	Mpa
Taber abraser	1000Cycles,1000g,CS-17Wheel	ASTMD1044	10.0	mg
Tensile modulus		ISO527-2/1	2350	Mpa
Tensile stress	Yield	ISO527-2/50	63.0	Mpa
Tensile stress	Tensile stress	Break	ISO527-2/50	65.0	Mpa
Tensile strain	Yield	ISO527-2/50	6.0	%
Tensile strain	Tensile strain	Break	ISO527-2/50	100	%

Thermal performance	Test Condition	Test Method	Test Result	Unit
RTIElec		UL746	130	°C
Evolution Calendar intelligent importer		UL746	130	°C
RTIStr		UL746	130	°C
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTMD648	129	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTMD648	137	°C
Linear coefficient of thermal expansion	MD：-40to95°C	ASTME831	6.8E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to80°C	ISO11359-2	7E-05	cm/cm/°C
Vicat softening temperature		ASTMD152510	154	°C
	Vicat softening temperature	--	ISO306/B50	140	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO306/B120	141	°C
specific heat		ASTMC351	1250	J/kg/°C
thermal conductivity		ASTMC177	0.19	W/m/K
thermal conductivity	thermal conductivity		ISO8302	0.20	W/m/K
BallPressure Test	125°C	IEC60695-10-2	Pass
Hot deformation temperature 9	1.8MPa,Unannealed,100mmSpan	ISO75-2/Ae	122	°C
Hot deformation temperature 9	Hot deformation temperature 9	0.45MPa,Unannealed,100mmSpan	ISO75-2/Be	133	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Hot wire ignition	HWI	UL746	PLC2
High arc combustion index	HAI	UL746	PLC1
High voltage arc tracing rate	HVTR	UL746	PLC2
Compared to the anti leakage trace index	CTI	UL746	PLC2
Dielectric strength	3.20mm,inAir	ASTMD149	15	KV/mm
Dielectric strength	Dielectric strength	3.20mm,in Oil	IEC60243-1	17	KV/mm
Relative permittivity	50Hz	IEC60250	2.70
	Relative permittivity	60Hz	IEC60250	2.70
	Relative permittivity	Relative permittivity	1MHz	IEC60250	2.70
Surface resistivity		IEC60093	>1.0E+15	ohms
Dielectric constant	50Hz	ASTMD150	3.17
	Dielectric constant	60Hz	ASTMD150	3.17
	Dielectric constant	Dielectric constant	1MHz	ASTMD150	2.96
Volume resistivity		ASTMD257	>1.0E+17	ohms·cm
Volume resistivity	Volume resistivity		IEC60093	>1.0E+15	ohms·cm
Dissipation factor	50Hz	ASTMD150	9E-04
	Dissipation factor	60Hz	ASTMD150	9E-04
		Dissipation factor	1MHz	ASTMD150	0.010
			Dissipation factor	50Hz	IEC60250	1E-03
				Dissipation factor	60Hz	IEC60250	1E-03
				Dissipation factor	Dissipation factor	1MHz	IEC60250	0.010

Impact performance	Test Condition	Test Method	Test Result	Unit
Dart impact equipped with measuring instruments	23°C,EnergyatPeakLoad	ASTMD3763	62.0	J
Falling hammer impact	23°C	ASTMD3029	169	J
Suspended wall beam gap impact strength 7	-30°C	ISO180/1A	10	kJ/m²
Suspended wall beam gap impact strength 7	Suspended wall beam gap impact strength 7	23°C	ISO180/1A	12	kJ/m²
Tensile impact strength 8		ASTMD1822	546	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Sale	ASTMD785	70
Rockwell hardness	Rockwell hardness	R-Sale	ASTMD785	118

optical performance	Test Condition	Test Method	Test Result	Unit
Refractive index		ASTMD542	1.586
Haze	2540µm	ASTMD1003	1.0	%
transmissivity	2540µm	ASTMD1003	88.0	%

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5mm	UL94	HB
Extreme Oxygen Index		ISO4589-2	25	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.