PC TARFLON™ LZ2510V IDEMITSU JAPAN
48
- Unit Price:
- $3537 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant UV resistance
- Application Areas:LCD application light-emitting diode
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 4.00 | cm3/10min |
| Shrinkage rate | TD:2.00mm | 内部方法 | 0.50to0.70 | % |
| MD:2.00mm | 内部方法 | 0.50to0.70 | % | |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.23 | % |
| Dissolved volume flow rate | MVR | ISO 1133 | 3 | cm3/10min |
| Shrinkage rate | TD | Internal Method | 0.5-0.7 | % |
| MD: 2.00 mm | Internal Method | 0.5-0.7 | % | |
| Water absorption rate | Equilibrium,23℃, 50% RH | ISO 62 | 0.23 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Yield | ISO 527-2 | 60 | Mpa |
| Fracture rate | ISO 527-2 | 80 | % | |
| Bending modulus | ISO 178 | 2300 | Mpa | |
| bending strength | ISO 178 | 100 | Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 40 | kJ/m² | |
| Tensile stress | Yield | ISO527-2 | 60.0 | Mpa |
| Nominal tensile fracture strain | ISO527-2 | 80 | % | |
| Bending modulus | ISO178 | 2300 | Mpa | |
| Bending stress | ISO178 | 100 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 129 | °C |
| Linear expansion coefficient - flow | ISO 11359-2 | 0.000065 | cm/cm/℃ | |
| Flame retardant grade | 1.00 mm | UL 94 | V-0 | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 129 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| RTIElec | UL746 | 80.0 | °C | |
| Evolution Calendar intelligent importer | UL746 | 80.0 | °C | |
| RTIStr | UL746 | 80.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the anti leakage trace index | CTI | UL746 | PLC3 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Sale | ISO2039-2 | 50 | |
| R-Sale | ISO2039-2 | 120 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 0.9mm | UL94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Shortcut | >PC< |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.