PC INFINO® NH-3200 K24333 Samsung Cheil South Korea
119
- Unit Price:
- $3228 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 28MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Glass fiber reinforced
- Application Areas:Laptop Electronic and Electrical Audio and video equipment
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | 250°C/5.0 kg | ASTM D1238, ISO 1133 | 19 | g/10 min |
| 300°C/1.2 kg | ASTM D1238, ISO 1133 | 12 | g/10 min | |
| Shrinkage rate | Flow : 3.20 mm | ASTM D955 | 0.10 到 0.40 | % |
| Across Flow : 3.20 mm | ASTM D955 | 0.10 到 0.40 | % | |
| Across Flow : 2.00 mm | ISO 294-4 | 0.10 到 0.40 | % | |
| 流量 : 2.00 mm | ISO 294-4 | 0.10 到 0.40 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | -- 3 | ASTM D638 | 4900 | Mpa |
| -- | ISO 527-2/5 | 5000 | Mpa | |
| Tensile strength | Yield 3 | ASTM D638 | 120 | Mpa |
| Yield | ISO 527-2/5 | 120 | Mpa | |
| Break 3 | ASTM D638 | 120 | Mpa | |
| Break | ISO 527-2/5 | 120 | Mpa | |
| elongation | Break 3 | ASTM D638 | 3.0 | % |
| Break | ISO 527-2/5 | 3.0 | % | |
| Bending modulus | -- 4 | ASTM D790 | 5900 | Mpa |
| -- 5 | ISO 178 | 6000 | Mpa | |
| bending strength | -- 4 | ASTM D790 | 150 | Mpa |
| -- 5 | ISO 178 | 150 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 105 | °C |
| 0.45 MPa, Unannealed, 4.00 mm | ISO 75-2/B | 102 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 100 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm | ISO 75-2/A | 97.0 | °C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot air dryer | 80 | °C | ||
| Vacuum drying machine | 80 | °C | ||
| Hot air dryer | 3.0 到 4.0 | hr | ||
| Vacuum drying machine | 4.0 到 6.0 | hr | ||
| Suggested maximum moisture content | 0.040 | % | ||
| Temperature at the rear of the barrel | 260 到 270 | °C | ||
| Temperature in the middle of the barrel | 270 到 290 | °C | ||
| Temperature at the front of the material cylinder | 260 到 280 | °C | ||
| Spray nozzle temperature | 270 | °C | ||
| Mold temperature | 60 到 70 | °C | ||
| Injection pressure | 98.1 | Mpa | ||
| Back pressure | 0.981 到 1.96 | Mpa | ||
| Screw speed | 30 到 100 | rpm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTM D785 | 120 | |
| R -Sale | ISO 2039-2 | 120 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75 mm | UL 94 | V-0 | |
| 0.8 to 3.0 mm | UL 94 | V-0 | ||
| 3.0 mm | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.