PC Makrolon® 2407 971000 COVESTRO GERMANY
119
- Unit Price:
- $2935 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 16MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low viscosity UV resistance High mobility Thermal stability Good demolding performanc
- Application Areas:Electrical field Electronic field Industrial applications Automotive sector currency currency
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | ISO1183 | 1.2 | g/cm³ | |
| Shrinkage rate | MD2.0mm | ISO294-4 | 0.65 | % |
| TD2.0mm | ISO294-4 | 0.70 | % | |
| Water absorption rate | (23°C,24hr) | ISO62 | 0.30 | % |
| (23°C,50RH) | ISO62 | 0.12 | % | |
| Melt flow index | 300℃/1.2Kg | ISO1133 | 19.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | 23°C | ISO527-2 | 66.0 | Mpa |
| elongation at break | 23°C | ISO527-2 | >50 | % |
| Tensile modulus | 23°C | ISO527-2 | 2400 | Mpa |
| Tensile creep modulus | 1Hr | ISO899-1 | 2200 | Mpa |
| 1000Hr | ISO899-1 | 1900 | Mpa | |
| bending strength | 23°C | ISO178 | 98.0 | Mpa |
| Bending modulus | 23°C | ISO178 | 2350 | Mpa |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 65 | kJ/m² |
| -30°C | ISO179/1eA | 14 | kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 75 | kJ/m² |
| -30°C | ISO180/1A | 12 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPaUnannealed | ISO75-2/Bf | 136 | °C |
| 1.80MPaAnnealed | ISO75-2/Af | 124 | °C | |
| Vicat softening temperature | ISO306/B50 | 143 | °C | |
| Coefficient of linear expansion | MD | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| TD | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistance | IEC60093 | 1E+15 | Ω.cm | |
| Surface resistance | IEC60093 | 1E+16 | Ω.cm | |
| Insulation strength | IEC60243-1 | 25 | KV/mm | |
| Dielectric constant | 23°C | IEC60250 | 3.00 | 1MHz |
| Dissipation factor | 23°C | IEC60250 | 5E-04 | 100HZ |
| 23°C | IEC60250 | 9E-03 | 1MHz | |
| 相对漏电起痕指数 | IEC60112 | 250 | V |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | ISO2039-1 | 116 | Mpa |
| Flame retardant performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Fire rating | UL-94 | 0.75mm | V-2 | |
| UL-94 | 1.50mm | V-2 | ||
| UL-94 | 2.60mm | V-2 | ||
| UL-94 | 2.70mm | HB | ||
| UL-94 | 3.00mm | HB | ||
| UL-94 | 6.00mm | HB | ||
| 氧指数 | ISO4589-2 | 27 | % |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ISO489 | 1.58 | °C | |
| Transmittance of 1000 μ m | ISO13468-2 | 89.0 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.