PC Makrolon® AL2647 550396 COVESTRO THAILAND
222
- Unit Price:
- $2864 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 54.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:transparent UV resistance
- Application Areas:Automotive sector Lighting fixtures
- Color:--
- Grade:Weather resistant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | 23°C | ISO1183 | 1.20 | g/cm³ |
| Apparent density 2 | ISO60 | 0.66 | g/cm³ | |
| Melt mass flow rate | 300°C/1.2kg | ISO1133 | 13 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 12.0 | cm3/10min |
| Shrinkage rate | TD | ISO2577 | 0.60to0.80 | % |
| MD | ISO2577 | 0.60to0.80 | % | |
| TD:2.00mm3 | ISO294-4 | 0.75 | % | |
| MD:2.00mm3 | ISO294-4 | 0.70 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.30 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.12 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2/1 | 2400 | Mpa |
| Tensile stress | Yield,23°C | ISO527-2/50 | 67.0 | Mpa |
| Break,23°C | ISO527-2/50 | 70.0 | Mpa | |
| Tensile strain | Yield,23°C | ISO527-2/50 | 6.1 | % |
| Break,23°C | ISO527-2/50 | 130 | % | |
| Nominal tensile fracture strain | 23°C | ISO527-2/50 | >50 | % |
| TensileCreepModule | 1hr | ISO899-1 | 2200 | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 1900 | Mpa |
| Bending modulus 4 | 23°C | ISO178 | 2400 | Mpa |
| Bending stress 4 | 3.5%Strain,23°C | ISO178 | 74.0 | Mpa |
| 23°C | ISO178 | 98.0 | Mpa | |
| Bending strain 5 | 23°C | ISO178 | 7.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal conductivity coefficient 9 | 23°C | ISO8302 | 0.20 | W/m/K |
| RTIElec | 1.5mm | UL746 | 125 | °C |
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 115 | °C |
| RTIStr | 1.5mm | UL746 | 125 | °C |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 136 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 123 | °C | |
| Glass transition temperature 8 | ISO11357-2 | 144 | °C | |
| Vicat softening temperature | -- | ISO306/B50 | 143 | °C |
| -- | ISO306/B120 | 144 | °C | |
| BallPressure Test | 135°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+16 | ohms | |
| Volume resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 34 | KV/mm |
| Relative permittivity | 23°C,100Hz | IEC60250 | 3.10 | |
| 23°C,1MHz | IEC60250 | 3.00 | ||
| Dissipation factor | 23°C,100Hz | IEC60250 | 5E-04 | |
| 23°C,1MHz | IEC60250 | 9E-03 | ||
| Leakage Trace Index | SolutionA | IEC60112 | 250 | V |
| SolutionB | IEC60112 | 125 | V |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| WaterVaporTransmission Rate | 23°C,85%RH,100µm | ISO15106-1 | 15 | g/m²/24hr |
| GasPermeation | CarbonDioxide:23°C,25.4µm | ISO2556 | 16900 | cm³/m²/bar/24hr |
| CarbonDioxide:23°C,100.0µm | ISO2556 | 3800 | cm³/m²/bar/24hr | |
| Nitrogen:23°C,25.4µm | ISO2556 | 510 | cm³/m²/bar/24hr | |
| Nitrogen:23°C,100.0µm | ISO2556 | 120 | cm³/m²/bar/24hr | |
| Oxygen:23°C,25.4µm | ISO2556 | 2760 | cm³/m²/bar/24hr | |
| Oxygen:23°C,100.0µm | ISO2556 | 670 | cm³/m²/bar/24hr |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Multi axis Instrumented Peak Impact Force | 23°C | ISO6603-2 | 5400 | N |
| Impact strength of simply supported beam gap 6 | -30°C,Complete Break | ISO7391 | 14 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 70 | kJ/m² | |
| Impact strength of simply supported beam without notch | -60°C | ISO179/1eU | NoBreak | |
| -30°C | ISO179/1eU | NoBreak | ||
| 23°C | ISO179/1eU | NoBreak | ||
| Suspended wall beam gap impact strength 7 | -30°C,Complete Break | ISO7391 | 15 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 70 | kJ/m² | |
| Multi axis Instrumented Impact Energy | -30°C | ISO6603-2 | 65.0 | J |
| 23°C | ISO6603-2 | 60.0 | J | |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO6603-2 | 6300 | N |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | ISO2039-1 | 115 | Mpa |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| transmissivity | 2000µm | ISO13468-2 | 89.0 | % |
| 3000µm | ISO13468-2 | 88.0 | % | |
| 4000µm | ISO13468-2 | >87.0 | % | |
| Haze | 3000µm | ISO14782 | <0.50 | % |
| Refractive Index11 | ISO489 | 1.587 | ||
| transmissivity | 1000µm | ISO13468-2 | 89.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 2.5mm | UL94 | HB | |
| 0.75mm | UL94 | V-2 | ||
| Extreme Oxygen Index 10 | ISO4589-2 | 28 | % | |
| FlashIgnitionTemperature | ASTMD1929 | 480 | °C | |
| SelfIgnition | ASTMD1929 | 550 | °C |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ElectrolyticalCorrosion | 23°C | IEC60426 | A1 | |
| ISO Shortcut | ISO7391-PC,MLR,(,,)-18-9 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.