PC LEXAN™ EXL1414 GY7D003 SABIC INNOVATIVE NANSHA
106
Unit Price:$3364 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 23MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Processability Moderate liquidity Ductility copolymer Good demolding performanc
- Application Areas:Bottle cap Home appliance components Electrical applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40to0.80 | % |
| TD：3.20mm | 内部方法 | 0.40to0.80 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.35 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % | |
| 熔体质量流动速率 | 300°C/1.2kg | ASTMD1238 | 10 | g/10min |
| Density/specific gravity | ASTMD792 | 1.18 | g/cm³ | |
| ISO1183 | 1.19 | g/cm³ | ||
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 9.00 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 770 | J/m |
| 23°C | ASTMD256 | 870 | J/m | |
| Elongation rate | Break | ASTMD638 | 98 | % |
| Bending modulus | ISO178 | 2250 | Mpa | |
| Unscented Izod Impact Strength | -30°C | ISO180/1U | NoBreak | |
| 23°C | ISO180/1U | NoBreak | ||
| Bending strength 5, | ISO178 | 85.0 | Mpa | |
| Impact strength of simply supported beam gap | -30°C | ISO179/1eA | 65 | kJ/m² |
| 23°C | ISO179/1eA | 70 | kJ/m² | |
| The impact strength of a simply supported beam without a notch is | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Suspended wall beam gap impact strength | -30°C | ISO180/1A | 60 | kJ/m² |
| 23°C | ISO180/1A | 70 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 70.0 | J |
| Elongation rate | Yield | ASTMD638 | 6.0 | % |
| Tensile modulus | ASTMD638 | 2020 | Mpa | |
| Tensile strength | Break | ASTMD638 | 50.3 | Mpa |
| Yield | ASTMD638 | 55.5 | Mpa | |
| Bending modulus | 50.0mmSpan | ASTMD790 | 2230 | Mpa |
| Bending strength | Yield,50.0mmSpan | ASTMD790 | 92.4 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 57.0 | Mpa |
| Break | ISO527-2/50 | 60.0 | Mpa | |
| Tensile strain | Yield | ISO527-2/50 | 6.0 | % |
| Break | ISO527-2/50 | 120 | % | |
| Tensile modulus | ISO527-2/1 | 2150 | Mpa | |
| Rockwell hardness | L-Sale | ASTMD785 | 89 | |
| R-Sale | ASTMD785 | 121 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 139 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 124 | °C | |
| RTIElec | UL746 | 130 | °C | |
| Evolution Calendar intelligent importer | UL746 | 120 | °C | |
| RTIStr | UL746 | 125 | °C | |
| Vicat softening temperature | ASTMD152510 | 145 | °C | |
| -- | ISO306/B50 | 145 | °C | |
| -- | ISO306/B120 | 146 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 7E-05 | cm/cm/°C |
| MD：23to80°C | ISO11359-2 | 7.2E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 7.5E-05 | cm/cm/°C | |
| TD：23to80°C | ISO11359-2 | 7.2E-05 | cm/cm/°C | |
| Hot deformation temperature | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 128 | °C |
| 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 140 | °C | |
| BallPressure Test | 125°C | IEC60695-10-2 | Pass |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 0.800mm,inOil | ASTMD149 | 16 | KV/mm |
| Dissipation factor | 100Hz | ASTMD150 | 1.2E-03 | |
| 1MHz | ASTMD150 | 9.3E-03 | ||
| Surface resistivity | ASTMD257 | >1.0E+15 | ohms | |
| Dielectric constant | 100Hz | ASTMD150 | 2.68 | |
| 1MHz | ASTMD150 | 2.64 | ||
| Volume resistivity | ASTMD257 | >1.0E+15 | ohms·cm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.40mm | UL94 | HB | |
| Burning wire flammability index | 0.8mm | IEC60695-2-12 | 850 | °C |
| 1.0mm | IEC60695-2-12 | 960 | °C | |
| Hot filament ignition temperature | 1.0mm | IEC60695-2-13 | 875 | °C |
| 3.0mm | IEC60695-2-13 | 875 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.