PC LUPOY® LD7701 LG CHEM KOREA
119
- Unit Price:
- $4099 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 36MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:Electrical/Electronic App Electrical field Electronic field Lighting diffuser Lighting applications Lighting installation
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD2.0mm | ASTMD995 | 0.60 | % |
| TD2.0mm | ASTMD995 | 0.60 | % | |
| Melt flow index | 300℃/1.2Kg | ASTMD1238 | 5.0 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | 23°C | ASTMD638 | 61.8 | Mpa |
| elongation at break | 23°C | ASTMD638 | >100 | % |
| bending strength | 23°C | ASTMD790 | 93.2 | Mpa |
| Bending modulus | 23°C | ASTMD790 | 2260 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.80MPaUnannealed | ASTMD648 | 125 | °C |
| Coefficient of linear expansion | MD | ASTMD696 | 6.8E-05 | cm/cm/°C |
| TD | ASTMD696 | 6.8E-05 | cm/cm/°C |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | ASTMD785 | 118 | R |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.