PC LEXAN™ HPS6 SABIC INNOVATIVE US
110
- Unit Price:
- $8934 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility
- Application Areas:medicine medical care
- Color:--
- Grade:Light diffusion level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：--2 | 内部方法 | 0.50to0.70 | % |
| MD：3.20mm | 内部方法 | 0.50to0.70 | % | |
| TD：3.20mm | 内部方法 | 0.50to0.70 | % | |
| Water absorption rate | 24hr | ASTMD570 | 0.15 | % |
| Saturation,23°C | ISO62 | 0.35 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % | |
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 7.0 | g/10min |
| 300°C/5.0kg | ASTMD1238 | 110 | g/10min | |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 6.50 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Elongation rate 4 | Break | ASTMD638 | 140 | % |
| Yield | ASTMD638 | 6.5 | % | |
| Bending modulus 5 | 50.0mmSpan | ASTMD790 | 2340 | Mpa |
| FlexuralStrength5 | Yield,50.0mmSpan | ASTMD790 | 97.9 | Mpa |
| Tensile strength 4 | Yield | ASTMD638 | 62.1 | Mpa |
| Bending strength 6,7 | ISO178 | 95.0 | Mpa | |
| Tensile modulus 3 | ASTMD638 | 2310 | Mpa | |
| Tensile strength 4 | Break | ASTMD638 | 68.9 | Mpa |
| Bending modulus 6 | ISO178 | 2250 | Mpa | |
| Tensile stress | Yield | ISO527-2/50 | 60.0 | Mpa |
| Break | ISO527-2/50 | 75.0 | Mpa | |
| Tensile strain | Yield | ISO527-2/50 | 6.0 | % |
| Break | ISO527-2/50 | 140 | % | |
| Tensile modulus | ISO527-2/1 | 2300 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 138 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 124 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 132 | °C | |
| 0.45MPa,Unannealed,3.20mm | ASTMD648 | 135 | °C | |
| Vicat softening temperature | ASTMD152511 | 154 | °C | |
| -- | ISO306/B50 | 143 | °C | |
| -- | ISO306/B120 | 140 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 6.2E-05 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 6E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 5.7E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 6E-05 | cm/cm/°C | |
| BallPressure Test | 75°C | IEC60695-10-2 | Pass | |
| Hot deformation temperature 10 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 124 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Simple supported beam without notch impact strength 8 | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Unscented Izod Impact Strength 9 | -30°C | ISO180/1U | NoBreak | |
| 23°C | ISO180/1U | NoBreak | ||
| Dart impact equipped with measuring instruments | 23°C,EnergyatPeakLoad | ASTMD3763 | 65.0 | J |
| 23°C,TotalEnergy | ASTMD3763 | 65.0 | J | |
| Impact strength of simply supported beam gap 8 | -30°C | ISO179/1eA | 15 | kJ/m² |
| 23°C | ISO179/1eA | 75 | kJ/m² | |
| Suspended wall beam gap impact strength 9 | -30°C | ISO180/1A | 10 | kJ/m² |
| 23°C | ISO180/1A | 70 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTMD785 | 118 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.