PC LEXAN™ EXL1492C NA8D017 SABIC INNOVATIVE US
95
Unit Price:$3517 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 16MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility Ductility at low temperat Short molding cycle
- Application Areas:Electronic and Electrical Aerospace Applications lens
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 熔体质量流动速率 | 300°C/1.2kg | ASTMD1238 | 10 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 9.00 | cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40to0.80 | % |
| TD：3.20mm | 内部方法 | 0.40to0.80 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.35 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ASTMD638 | 2020 | Mpa | |
| ISO527-2/1 | 2150 | Mpa | ||
| Tensile strength | Yield | ASTMD638 | 55.5 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 57.0 | Mpa |
| Impact strength of simply supported beam gap | -30°C | ISO179/1eA | 65 | kJ/m² |
| 23°C | ISO179/1eA | 70 | kJ/m² | |
| The impact strength of a simply supported beam without a notch is | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Suspended wall beam gap impact strength | -30°C | ISO180/1A | 60 | kJ/m² |
| 23°C | ISO180/1A | 70 | kJ/m² | |
| Unscented Izod Impact Strength | -30°C | ISO180/1U | NoBreak | |
| 23°C | ISO180/1U | NoBreak | ||
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 70.0 | J |
| Rockwell hardness | L-Sale | ASTMD785 | 89 | |
| R-Sale | ASTMD785 | 121 | ||
| Tensile strength | Break | ASTMD638 | 50.3 | Mpa |
| Tensile stress | Break | ISO527-2/50 | 60.0 | Mpa |
| Elongation rate | Yield | ASTMD638 | 6.0 | % |
| Tensile strain | Yield | ISO527-2/50 | 6.0 | % |
| Elongation rate | Break | ASTMD638 | 98 | % |
| Tensile strain | Break | ISO527-2/50 | 120 | % |
| Bending modulus | 50.0mmSpan | ASTMD790 | 2230 | Mpa |
| ISO178 | 2250 | Mpa | ||
| Bending strength 5, | ISO178 | 85.0 | Mpa | |
| Bending strength | Yield,50.0mmSpan | ASTMD790 | 92.4 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 7E-05 | cm/cm/°C |
| MD：23to80°C | ISO11359-2 | 7.2E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 7.5E-05 | cm/cm/°C | |
| TD：23to80°C | ISO11359-2 | 7.2E-05 | cm/cm/°C | |
| RTIElec | UL746 | 130 | °C | |
| Evolution Calendar intelligent importer | UL746 | 120 | °C | |
| RTIStr | UL746 | 125 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 139 | °C |
| 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 140 | °C | |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 124 | °C | |
| 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 128 | °C | |
| Vicat softening temperature | ASTMD152510 | 145 | °C | |
| -- | ISO306/B50 | 145 | °C | |
| -- | ISO306/B120 | 146 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 0.800mm,inOil | ASTMD149 | 16 | KV/mm |
| Dielectric constant | 100Hz | ASTMD150 | 2.68 | |
| 1MHz | ASTMD150 | 2.64 | ||
| Dissipation factor | 100Hz | ASTMD150 | 1.2E-03 | |
| 1MHz | ASTMD150 | 9.3E-03 | ||
| Surface resistivity | ASTMD257 | >1.0E+15 | ohms | |
| Volume resistivity | ASTMD257 | >1.0E+15 | ohms·cm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning wire flammability index | 0.8mm | IEC60695-2-12 | 850 | °C |
| 1.0mm | IEC60695-2-12 | 960 | °C | |
| Hot filament ignition temperature | 1.0mm | IEC60695-2-13 | 875 | °C |
| 3.0mm | IEC60695-2-13 | 875 | °C | |
| Extreme Oxygen Index | ISO4589-2 | 37 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.