PC LEXAN™ 1414T SABIC INNOVATIVE SHANGHAI
122
- Unit Price:
- $3816 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 50MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low temperature resistanc transparent Easy to process Middle flow
- Application Areas:Electrical field Electronic field Household appliances Fitness equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40to0.80 | % |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.15 | % |
| Saturation,23°C | ISO62 | 0.35 | % | |
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 10 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 9.00 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Elongation rate 3 | Yield | ASTMD638 | 6.0 | % |
| Tensile modulus 2 | ASTMD638 | 2020 | Mpa | |
| Tensile strength 3 | Yield | ASTMD638 | 55.5 | Mpa |
| Break | ASTMD638 | 50.3 | Mpa | |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 2230 | Mpa |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 92.4 | Mpa |
| Tensile stress | Break | ISO527-2/50 | 60.0 | Mpa |
| Yield | ISO527-2/50 | 57.0 | Mpa | |
| Tensile strain | Yield | ISO527-2/50 | 6.0 | % |
| Break | ISO527-2/50 | 120 | % | |
| Tensile modulus | ISO527-2/1 | 2150 | Mpa | |
| Elongation rate 4 | Break | ASTMD638 | 98 | % |
| Bending modulus 5 | ISO178 | 2250 | Mpa | |
| Bending strength 5,6 | ISO178 | 85.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature 9 | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 128 | °C |
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 139 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 124 | °C | |
| Vicat softening temperature | ASTMD152510 | 145 | °C | |
| -- | ISO306/B50 | 145 | °C | |
| -- | ISO306/B120 | 146 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 7E-05 | cm/cm/°C |
| MD：23to80°C | ISO11359-2 | 7.2E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 7.5E-05 | cm/cm/°C | |
| TD：23to80°C | ISO11359-2 | 7.2E-05 | cm/cm/°C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 70.0 | J |
| Unscented Izod Impact Strength 8 | -30°C | ISO180/1U | NoBreak | |
| 23°C | ISO180/1U | NoBreak | ||
| Impact strength of simply supported beam gap 7 | 23°C | ISO179/1eA | 70 | kJ/m² |
| -30°C | ISO179/1eA | 65 | kJ/m² | |
| The impact strength of a simply supported beam without a notch is 7 | 23°C | ISO179/1eU | NoBreak | |
| -30°C | ISO179/1eU | NoBreak | ||
| Suspended wall beam gap impact strength 8 | -30°C | ISO180/1A | 60 | kJ/m² |
| 23°C | ISO180/1A | 70 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.