PC Makrolon® ET3113 550115 COVESTRO THAILAND

122

Unit Price:
$2148 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
15MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Weather resistance Hydrolysis resistance
Application Areas:PC board Electrical field Electronic field Other sheets Automotive sector
Color:--
Grade:Extrusion grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	Across Flow	ISO 2577	0.60 到 0.80	%
	Shrinkage rate	流量	ISO 2577	0.60 到 0.80	%
		Shrinkage rate	Across Flow : 280°C, 2.00 mm 4	ISO 294-4	0.75	%
		Shrinkage rate	Shrinkage rate	流量 : 2.00 mm 4	ISO 294-4	0.70	%
Water absorption rate	Saturation, 23°C	ISO 62	0.30	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.12	%
Melt flow rate	300°C/1.2 kg	ISO 1133	6.5	g/10 min
Molten Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	6.00	cm3/10min
Apparent density 3		ISO 60	0.66	g/cm³
density	23°C	ISO 1183	1.20	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Flexural Strain at Flexural Strength	23°C	ISO 178	7.2	%
Bending stress 5	23°C	ISO 178	96.0	Mpa
Bending stress 5	Bending stress 5	3.5% Strain, 23°C	ISO 178	72.0	Mpa
Nominal tensile fracture strain	23°C	ISO 527-2/50	> 50	%
Tensile stress	Yield, 23°C	ISO 527-2/50	65.0	Mpa
Tensile stress	Tensile stress	Break, 23°C	ISO 527-2/50	70.0	Mpa
Tensile strain	Yield, 23°C	ISO 527-2/50	6.3	%
Tensile strain	Tensile strain	Break, 23°C	ISO 527-2/50	130	%
Tensile creep modulus	1 hr	ISO 899-1	2200	Mpa
Tensile creep modulus	Tensile creep modulus	1000 hr	ISO 899-1	1900	Mpa
Tensile modulus	23°C	ISO 527-2/1	2350	Mpa
Bending modulus	23°C	ISO 178	2350	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	141	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	128	°C
RTI	1.5 mm	UL 746	125	°C
RTI Imp	1.5 mm	UL 746	115	°C
RTI Elec	1.5 mm	UL 746	125	°C
thermal conductivity	23°C	ISO 8302	0.20	W/m/K
Vicat softening temperature	--	ISO 306/B50	148	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	149	°C
Linear coefficient of thermal expansion	Flow : 23 to 55°C	ISO 11359-2	6.5E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 55°C	ISO 11359-2	6.5E-5	cm/cm/°C
Glass transition temperature 8		ISO 11357-2	148	°C
Ball Pressure Test	140°C	IEC 60695-10-2	通过

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric strength	23°C, 1.00 mm	IEC 60243-1	34	KV/mm
Relative permittivity	23°C, 100 Hz	IEC 60250	3.10
Relative permittivity	Relative permittivity	23°C, 1 MHz	IEC 60250	3.00
Leakage Trace Index	Solution A	IEC 60112	250	V
Leakage Trace Index	Leakage Trace Index	Solution B	IEC 60112	125	V
Dissipation factor	23°C, 100 Hz	IEC 60250	8.0E-4
Dissipation factor	Dissipation factor	23°C, 1 MHz	IEC 60250	0.010
Surface resistivity		IEC 60093	1.0E+16	ohms
Volume resistivity	23°C	IEC 60093	1.0E+16	ohms·cm

film	Test Condition	Test Method	Test Result	Unit
Water vapor permeability	23°C, 85% RH, 100 µm	ISO 15106-1	15	g/m²/24 hr
Carbon Dioxide Permeability	23°C, 25.4 µm	ISO 2556	16900	cm³/m²/bar/24 hr
Gas Permeation	Carbon Dioxide : 100.0 µm	ISO 2556	3800	cm³/m²/bar/24 hr
	Gas Permeation	Nitrogen : 25.4 µm	ISO 2556	510	cm³/m²/bar/24 hr
		Gas Permeation	Nitrogen : 100.0 µm	ISO 2556	120	cm³/m²/bar/24 hr
			Gas Permeation	Oxygen : 25.4 µm	ISO 2556	2760	cm³/m²/bar/24 hr
			Gas Permeation	Gas Permeation	Oxygen : 100.0 µm	ISO 2556	650	cm³/m²/bar/24 hr

Impact performance	Test Condition	Test Method	Test Result	Unit
Suspended wall beam gap impact strength 7	-30°C, Complete Break	ISO 180/A	20	kJ/m²
Suspended wall beam gap impact strength 7	Suspended wall beam gap impact strength 7	23°C, Partial Break	ISO 180/A	70	kJ/m²
Impact strength of simply supported beam gap 7	-30°C, Complete Break	ISO 179/1eA	18	kJ/m²
Impact strength of simply supported beam gap 7	Impact strength of simply supported beam gap 7	23°C, Partial Break	ISO 179/1eA	80	kJ/m²
Multi axis Instrumented Impact Energy	-30°C	ISO 6603-2	70.0	J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	60.0	J
Multi axis Instrumented Peak Impact Force	-30°C	ISO 6603-2	6500	N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	5600	N
Impact strength of simply supported beam without notch	-60°C	ISO 179/1eU	无断裂
	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂

hardness	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness		ISO 2039-1	113	Mpa

optical performance	Test Condition	Test Method	Test Result	Unit
Refractive index 15		ISO 489	1.587
Electrolytical Corrosion	23°C	IEC 60426	A1
ISO 9660			ISO 7391-PC,EL,(,,)-09-9
transmissivity	1000 µm	ISO 13468-2	89.0	%
	transmissivity	2000 µm	ISO 13468-2	89.0	%
		transmissivity	3000 µm	ISO 13468-2	88.0	%
		transmissivity	transmissivity	4000 µm	ISO 13468-2	87.0	%
Haze	3000 µm	ISO 14782	< 0.80	%

flammability	Test Condition	Test Method	Test Result	Unit
Extreme Oxygen Index 10		ISO 4589-2	28	%
Flash Ignition Temperature		ASTM D1929	480	°C
Needle Flame Test	1.50 mm 12	IEC 60695-11-5	1.0	min
	Needle Flame Test	2.00 mm 12	IEC 60695-11-5	2.0	min
		Needle Flame Test	2.00 mm 13	IEC 60695-11-5	0.1	min
			Needle Flame Test	3.00 mm 12	IEC 60695-11-5	2.0	min
			Needle Flame Test	Needle Flame Test	3.00 mm 13	IEC 60695-11-5	0.2	min
Self Ignition Temperature		ASTM D1929	550	°C
Burning wire flammability index	0.75 mm	IEC 60695-2-12	875	°C
	Burning wire flammability index	1.5 mm	IEC 60695-2-12	875	°C
	Burning wire flammability index	Burning wire flammability index	3.0 mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	0.75 mm	IEC 60695-2-13	875	°C
	Hot filament ignition temperature	1.5 mm	IEC 60695-2-13	875	°C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	900	°C
Burning rate	> 1.00 mm	ISO 3795	passed
UL flame retardant rating	1.5 mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	0.75 mm	UL 94	V-2
Application of Flame from Small Burner 11		DIN 53438-1, -3	K1, F1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.