PC LUPOY® 1201-05 LG CHEM KOREA
122
- Unit Price:
- $3072 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 44.3MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:transparent wear resistant Low viscosity
- Application Areas:packing bottle Food containers Toy
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | ASTM D792 | 1.20 | g/cm³ | |
| Melt flow rate | 300°C/1.2 kg | ASTM D1238 | 5.0 | g/10 min |
| Shrinkage rate - flow | ASTM D955 | 0.50 到 0.70 | % | |
| Water absorption rate | 24 hr, 23°C | ASTM D570 | 0.15 | % |
| Equilibrium, 23°C, 50% RH | ASTM D570 | 0.32 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ASTM D638 | 2410 | Mpa | |
| Tensile strength | Yield, 23°C 3 | ASTM D638 | 60.0 | Mpa |
| Break | ASTM D638 | 72.0 | Mpa | |
| elongation | Yield | ASTM D638 | 6.0 | % |
| Break | ASTM D638 | 150 | % | |
| Bending modulus | ASTM D790 | 2410 | Mpa | |
| bending strength | ASTM D790 | 96.0 | Mpa | |
| Wear resistance - Delta Haze 4 | ASTM D1004 | 45 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal deformation temperature under load | 0.45 MPa, Annealed, 4.00 mm | ASTM D648 | 146 | °C |
| 1.8 MPa, Unannealed, 4.00 mm | ASTM D648 | 132 | °C | |
| 1.8 MPa, Annealed, 4.00 mm | ASTM D648 | 143 | °C | |
| Vicat softening temperature | ASTM D15257 | 151 | °C | |
| Ball pressure temperature | IEC 60598-1 | > 125 | °C | |
| Linear coefficient of thermal expansion - flow | -40 to 82°C | ASTM D696 | 6.8E-5 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | 23°C | ASTM D257 | 2.0E+17 | ohms·cm |
| Dielectric strength | ASTM D149 | 17 | KV/mm | |
| Dielectric constant | 60 Hz | ASTM D150 | 3.00 | |
| Dissipation factor | 60 Hz | ASTM D150 | 1.0E-3 | |
| Leakage Trace Index | 2.00 mm | IEC 60112 | 250 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C, 3.18 mm | ASTM D256 | 950 | J/m |
| Non notched cantilever beam impact | 23°C | ASTM D256 | 无断裂 | |
| Dart impact equipped with measuring instruments | 23°C, 3.18 mm, Total Energy | ASTM D3763 | 94.0 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Scale | ASTM D785 | 74 | |
| R-Scale | ASTM D785 | 118 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ASTM D542 | 1.586 | ||
| transmissivity | ASTM D1003 | 89.0 | % | |
| Haze | ASTM D1003 | 0.70 到 1.5 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 3.0 mm | UL 94 | HB | |
| 0.50 mm | UL 94 | V-2 | ||
| 1.6 mm | UL 94 | V-2 | ||
| 2.5 to 2.7 mm | UL 94 | V-2 | ||
| Hot filament ignition temperature | 2.0 mm, 5.0 sec | IEC 60695-2-13 | 850 | °C |
| Extreme Oxygen Index | ASTM D2863 | 26 | % | |
| Average degree of combustion | ASTM D635 | 3 | CM |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.