Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Specific volume | | ASTMD792 | 0.835 | cm³/g |
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 15 | g/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Water absorption rate | 24hr | ASTMD570 | 0.15 | % |
| Water absorption rate | Equilibrium,23°C | ASTMD570 | 0.35 | % |
| Water absorption rate | Equilibrium,100°C | ASTMD570 | 0.58 | % |
| Outdoor applicability | | UL746C | f1 | |
| Outdoor applicability | | UL746C | f1 | |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength 2 | Yield | ASTMD638 | 62.1 | Mpa |
| Tensile strength 2 | Break | ASTMD638 | 55.8 | Mpa |
| Elongation rate 2 | Yield | ASTMD638 | 7.0 | % |
| Elongation rate 2 | Break | ASTMD638 | 90 | % |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 2240 | Mpa |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 91.0 | Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | ASTMD1044 | 10.0 | mg |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | | ASTMD15255 | 152 | °C |
| Linear coefficient of thermal expansion | MD：-40to95°C | ASTME831 | 6.8E-05 | cm/cm/°C |
| thermal conductivity | | ASTMC177 | 0.19 | W/m/K |
| RTIElec | | UL746 | 130 | °C |
| Evolution Calendar intelligent importer | | UL746 | 120 | °C |
| RTIStr | | UL746 | 130 | °C |
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 138 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 132 | °C |
| thermal conductivity | | ASTMC177 | 0.19 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistivity | | ASTMD257 | >1.0E+17 | ohms·cm |
| Arc resistance 6 | | ASTMD495 | PLC7 | |
| Dielectric constant | 1MHz | ASTMD150 | 2.96 | |
| Dissipation factor | 50Hz | ASTMD150 | 9E-04 | |
| Dissipation factor | 60Hz | ASTMD150 | 9E-04 | |
| Dissipation factor | 1MHz | ASTMD150 | 0.010 | |
| Arc resistance 6 | | ASTMD495 | PLC7 | |
| Compared to the anti leakage trace index | CTI | UL746 | PLC3 | |
| High arc combustion index | HAI | UL746 | PLC2 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC3 | |
| Hot wire ignition | HWI | UL746 | PLC2 | |
| Volume resistivity | | ASTMD257 | >1.0E+17 | ohms·cm |
| Dielectric strength | 3.20mm,inAir | ASTMD149 | 17 | KV/mm |
| Dielectric constant | 50Hz | ASTMD150 | 3.01 | |
| Dielectric constant | 60Hz | ASTMD150 | 3.01 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Falling hammer impact | 23°C | ASTMD3029 | 169 | J |
| Tensile impact strength 4 | | ASTMD1822 | 525 | kJ/m² |
| Tensile impact strength 4 | | ASTMD1822 | 525 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M-Sale | ASTMD785 | 70 | |
| Rockwell hardness | R-Sale | ASTMD785 | 118 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Refractive index | | ASTMD542 | 1.586 | |
| transmissivity | 2540µm | ASTMD1003 | 85.0 | % |
| Haze | 2540µm | ASTMD1003 | 1.0 | % |
| Refractive index | | ASTMD542 | 1.586 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 3.0mm | UL94 | V-0 | |
| UL flame retardant rating | 1.5mm | UL94 | V-2 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.