PC Makrolon® 6555 901510 COVESTRO THAILAND
138
Unit Price:$2888 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 16MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Medium viscosity
- Application Areas:Electrical field Electronic field Industrial applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 密度 / 比重 | 23°C | ISO1183 | 1.20 | g/cm³ |
| 表观密度 | ISO60 | 0.64 | g/cm³ | |
| 熔体质量流动速率 | 300°C/1.2kg | ISO1133 | 10 | g/10min |
| 熔体体积流动速率 | 300°C/1.2kg | ISO1133 | 10.0 | cm3/10min |
| 收缩率 | TD | ISO2577 | 0.60to0.80 | % |
| MD | ISO2577 | 0.60to0.80 | % | |
| TD:2.00mm3 | ISO294-4 | 0.75 | % | |
| MD:2.00mm3 | ISO294-4 | 0.70 | % | |
| 吸水率 | 饱和,23°C | ISO62 | 0.30 | % |
| 平衡,23°C,50%RH | ISO62 | 0.12 | % |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 简支梁缺口冲击强度 | -30°C,完全断裂 | ISO7391 | 14 | kJ/m² |
| 23°C,局部断裂 | ISO7391 | 70 | kJ/m² | |
| 简支梁无缺口冲击强度 | -60°C | ISO179/1eU | NoBreak | |
| -30°C | ISO179/1eU | NoBreak | ||
| 23°C | ISO179/1eU | NoBreak | ||
| 悬壁梁缺口冲击强度 | -30°C,完全断裂 | ISO7391 | 12 | kJ/m² |
| 23°C,局部断裂 | ISO7391 | 65 | kJ/m² | |
| 多轴向仪器化冲击能量 | -30°C | ISO6603-2 | 65.0 | J |
| 23°C | ISO6603-2 | 60.0 | J | |
| 多轴向仪器化冲击力峰值 | -30°C | ISO6603-2 | 6300 | N |
| 23°C | ISO6603-2 | 5400 | N | |
| 弯曲应力 | 23°C | ISO178 | 98.0 | Mpa |
| 弯曲应变 | 23°C | ISO178 | 7.1 | % |
| 球压硬度 | ISO2039-1 | 115 | Mpa | |
| 拉伸模量 | 23°C | ISO527-2/1 | 2400 | Mpa |
| 拉伸应力 | 屈服,23°C | ISO527-2/50 | 66.0 | Mpa |
| 断裂,23°C | ISO527-2/50 | 70.0 | Mpa | |
| 拉伸应变 | 屈服,23°C | ISO527-2/50 | 6.2 | % |
| 断裂,23°C | ISO527-2/50 | 130 | % | |
| 标称拉伸断裂应变 | 23°C | ISO527-2/50 | >50 | % |
| TensileCreepModulus | 1hr | ISO899-1 | 2200 | Mpa |
| 拉伸蠕变模量 | 1000hr | ISO899-1 | 1900 | Mpa |
| 弯曲模量 | 23°C | ISO178 | 2400 | Mpa |
| 弯曲应力 | 3.5%Strain,23°C | ISO178 | 74.0 | Mpa |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 热变形温度 | 0.45MPa,未退火 | ISO75-2/B | 137 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 125 | °C | |
| 玻璃转化温度 | ISO11357-2 | 145 | °C | |
| 维卡软化温度 | -- | ISO306/B50 | 144 | °C |
| -- | ISO306/B120 | 145 | °C | |
| BallPressureTest | 136°C | IEC60695-10-2 | Pass | |
| 线形热膨胀系数 | MD：23到55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C | |
| 导热系数 | 23°C | ISO8302 | 0.20 | W/m/K |
| RTIElec | 1.5mm | UL746 | 125 | °C |
| RTIImp | 1.5mm | UL746 | 115 | °C |
| RTIStr | 1.5mm | UL746 | 125 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 表面电阻率 | IEC60093 | 1E+16 | ohms | |
| 体积电阻率 | 23°C | IEC60093 | 1E+16 | ohms·cm |
| 介电强度 | 23°C,1.00mm | IEC60243-1 | 34 | KV/mm |
| 相对电容率 | 23°C,100Hz | IEC60250 | 3.10 | |
| 23°C,1MHz | IEC60250 | 3.00 | ||
| 耗散因数 | 23°C,100Hz | IEC60250 | 8E-04 | |
| 23°C,1MHz | IEC60250 | 9E-03 | ||
| 漏电起痕指数 | 解决方案A | IEC60112 | 225 | V |
| 解决方案B | IEC60112 | 125 | V |
| 薄膜 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| WaterVaporTransmissionRate | 23°C,85%RH,100µm | ISO15106-1 | 15 | g/m²/24hr |
| GasPermeation | CarbonDioxide:23°C,25.4µm | ISO2556 | 16900 | cm³/m²/bar/24hr |
| CarbonDioxide:23°C,100.0µm | ISO2556 | 4300 | cm³/m²/bar/24hr | |
| Nitrogen:23°C,25.4µm | ISO2556 | 510 | cm³/m²/bar/24hr | |
| Nitrogen:23°C,100.0µm | ISO2556 | 130 | cm³/m²/bar/24hr | |
| Oxygen:23°C,25.4µm | ISO2556 | 2760 | cm³/m²/bar/24hr | |
| Oxygen:23°C,100.0µm | ISO2556 | 700 | cm³/m²/bar/24hr |
| 光学性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 折射率 | ISO489 | 1.586 | ||
| 透光率 | 1000µm | ISO13468-2 | 89.0 | % |
| 2000µm | ISO13468-2 | 89.0 | % | |
| 3000µm | ISO13468-2 | 88.0 | % | |
| 4000µm | ISO13468-2 | 87.0 | % |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL阻燃等级 | 1.0mm | UL94 | V-2 | |
| 3.0mm | UL94 | V-0 | ||
| 灼热丝易燃指数 | 0.75mm | IEC60695-2-12 | 875 | °C |
| 1.5mm | IEC60695-2-12 | 960 | °C | |
| 3.0mm | IEC60695-2-12 | 960 | °C | |
| 热灯丝点火温度 | 0.75mm | IEC60695-2-13 | 875 | °C |
| 1.5mm | IEC60695-2-13 | 875 | °C | |
| 3.0mm | IEC60695-2-13 | 875 | °C | |
| 极限氧指数 | ISO4589-2 | 35 | % | |
| ApplicationofFlamefromSmallBurner-MethodKandF | 2.00mm | DIN53438-1,-3 | K1,F1 | |
| 燃烧速率-US-FMVSS | >1.00mm | ISO3795 | passed | |
| FlashIgnitionTemperature | ASTMD1929 | 460 | °C | |
| GlowWireTest | 1.50mm | EDFHN60E.02 | 750 | °C |
| 3.00mm | EDFHN60E.02 | 750 | °C | |
| 针焰试验 | MethodF:1.50mm | IEC60695-11-5 | 2.0 | min |
| MethodF:2.00mm | IEC60695-11-5 | 2.0 | min | |
| MethodF:3.00mm | IEC60695-11-5 | 2.0 | min | |
| MethodK:1.50mm | IEC60695-11-5 | 1.0 | min | |
| MethodK:2.00mm | IEC60695-11-5 | 2.0 | min | |
| MethodK:3.00mm | IEC60695-11-5 | 2.0 | min | |
| SelfIgnitionTemperature | ASTMD1929 | 530 | °C |
| 补充信息 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ElectrolyticalCorrosion | 23°C | IEC60426 | A1 | |
| ISOShortname | ISO7391-PC,MFR,(,,)-09-9 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.