PC Makrolon® 6487 COVESTRO THAILAND
132
- Unit Price:
- $3136 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Good demolding performanc Medium viscosity Flame retardant High impact resistance UV curing Processability
- Application Areas:Electrical field Electronic field Household appliances Household appliances Architectural application Automotive sector Barrel disposable Medical Supplies
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO2577 | 0.60to0.80 | % |
| MD | ISO2577 | 0.60to0.80 | % | |
| TD:2.00mm3 | ISO294-4 | 0.75 | % | |
| MD:2.00mm3 | ISO294-4 | 0.70 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.30 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.12 | % | |
| Melt mass flow rate | 300°C/1.2kg | ISO1133 | 10 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 9.00 | cm3/10min |
| Density/specific gravity | 23°C | ISO1183 | 1.20 | g/cm³ |
| Apparent density 2 | ISO60 | 0.64 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Nominal tensile fracture strain | 23°C | ISO527-2/50 | >50 | % |
| Bending strain 5 | 23°C | ISO178 | 7.0 | % |
| Bending stress 4 | 3.5%Strain,23°C | ISO178 | 75.0 | Mpa |
| 23°C | ISO178 | 99.0 | Mpa | |
| Bending modulus 4 | 23°C | ISO178 | 2450 | Mpa |
| Tensile stress | Yield,23°C | ISO527-2/50 | 66.0 | Mpa |
| Break,23°C | ISO527-2/50 | 65.0 | Mpa | |
| Tensile strain | Yield,23°C | ISO527-2/50 | 6.0 | % |
| Break,23°C | ISO527-2/50 | 120 | % | |
| Tensile modulus | 23°C | ISO527-2/1 | 2450 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 134 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 122 | °C | |
| RTIElec | 1.5mm | UL746 | 125 | °C |
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 115 | °C |
| RTIStr | 1.5mm | UL746 | 125 | °C |
| Vicat softening temperature | -- | ISO306/B50 | 143 | °C |
| -- | ISO306/B120 | 141 | °C | |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C | |
| Glass transition temperature 8 | ISO11357-2 | 141 | °C | |
| Thermal conductivity coefficient 9 | 23°C | ISO8302 | 0.20 | W/m/K |
| BallPressure Test | 135°C | IEC60695-10-2 | Pass |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 34 | KV/mm |
| Relative permittivity | 23°C,100Hz | IEC60250 | 3.10 | |
| 23°C,1MHz | IEC60250 | 3.00 | ||
| Leakage Trace Index | SolutionA | IEC60112 | 225 | V |
| SolutionB | IEC60112 | 125 | V | |
| Dissipation factor | 23°C,100Hz | IEC60250 | 8E-04 | |
| 23°C,1MHz | IEC60250 | 9E-03 | ||
| Surface resistivity | IEC60093 | 1E+16 | ohms | |
| Volume resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Multi axis Instrumented Impact Energy | -30°C | ISO6603-2 | 55.0 | J |
| 23°C | ISO6603-2 | 50.0 | J | |
| Suspended wall beam gap impact strength 7 | -30°C,Complete Break | ISO7391 | 12 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 65 | kJ/m² | |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO6603-2 | 6000 | N |
| 23°C | ISO6603-2 | 5200 | N | |
| Impact strength of simply supported beam gap 6 | -30°C,Complete Break | ISO7391 | 12 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 70 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | ISO2039-1 | 117 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-0 | |
| 3.0mm | UL94 | 5VA | ||
| Burning wire flammability index | 1.5mm | IEC60695-2-12 | 960 | °C |
| 3.0mm | IEC60695-2-12 | 960 | °C | |
| Hot filament ignition temperature | 1.5mm | IEC60695-2-13 | 900 | °C |
| 3.0mm | IEC60695-2-13 | 930 | °C | |
| Burning rate - US-FMVSS | >1.00mm | ISO3795 | passed | |
| FlashIgnitionTemperature | ASTMD1929 | 470 | °C | |
| Extreme Oxygen Index 10 | ISO4589-2 | 36 | % | |
| SelfIgnition | ASTMD1929 | 550 | °C | |
| ApplicationofFlamefromSmallBurner MethodKandF | 2.00mm | DIN53438-1,-3 | K1,F1 |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Shortcut | ISO7391-PC,MFLR,(,,)-09-9 | |||
| ElectrolyticalCorrosion | 23°C | IEC60426 | A1 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.