Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | 24 hr | ASTM D570 | 0.19 | % |
| Melt flow rate | 300°C/1.2 kg | ASTM D1238 | 2.0 | g/10 min |
| Melt flow rate | 300°C/6.1 kg | ASTM D1238 | 9.0 | g/10 min |
| Specific volume | | ASTM D792 | 0.830 | cm³/g |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.80 到 1.0 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| elongation | Break | ASTM D638 | 78 | % |
| Bending modulus | 50.0 mm Span | ASTM D790 | 2330 | Mpa |
| bending strength | Yield, 50.0 mm Span | ASTM D790 | 97.0 | Mpa |
| Tensile strength 1 | Yield | ASTM D638 | 65.0 | Mpa |
| Tensile strength 1 | Break | ASTM D638 | 77.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| specific heat | | ASTM C351 | 1260 | J/kg/°C |
| thermal conductivity | | ASTM C177 | 0.21 | W/m/K |
| RTI | | UL 746 | 130 | °C |
| RTI Imp | | UL 746 | 130 | °C |
| RTI Elec | | UL 746 | 130 | °C |
| Linear coefficient of thermal expansion - flow | -40 to 95°C | ASTM E831 | 8.1E-5 | cm/cm/°C |
| Thermal deformation temperature under load | 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 148 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 3 | |
| Hot wire ignition (HWI) | | UL 746 | PLC 2 | |
| High arc combustion index (HAI) 5 | | UL 746 | PLC 3 | |
| Dissipation factor | 50 Hz | ASTM D150 | 1.6E-3 | |
| Dissipation factor | 60 Hz | ASTM D150 | 1.6E-3 | |
| Dissipation factor | 100 Hz | ASTM D150 | 0.026 | |
| Dielectric strength | 3.20 mm, in Air | ASTM D149 | 20 | KV/mm |
| Dielectric constant | 60 Hz | ASTM D150 | 3.27 | |
| Dielectric constant | 50 kHz | ASTM D150 | 3.27 | |
| Dielectric constant | 1 MHz | ASTM D150 | 3.10 | |
| Volume resistivity | | ASTM D257 | > 2.5E+17 | ohms·cm |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 3 | |
| Arc resistance 4 | | ASTM D495 | PLC 6 | |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|
| drying temperature | | | 120 | °C |
| Suggested maximum moisture content | | | 0.020 | % |
| Processing (melt) temperature | | | 350 到 370 | °C |
| Mold temperature | | | 80 到 115 | °C |
| drying time | | | 3.0 到 4.0 | hr |
| Suggested injection volume | | | 40 到 60 | % |
| Temperature at the rear of the barrel | | | 325 到 350 | °C |
| Temperature in the middle of the barrel | | | 340 到 360 | °C |
| Temperature at the front of the material cylinder | | | 350 到 370 | °C |
| Spray nozzle temperature | | | 345 到 365 | °C |
| Back pressure | | | 0.300 到 0.700 | Mpa |
| Screw speed | | | 40 到 70 | rpm |
| Exhaust hole depth | | | 0.025 到 0.076 | mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile impact strength 3 | | ASTM D1822 | 577 | kJ/m² |
| Falling hammer impact | 23°C | ASTM D3029 | 149 | J |
| Non notched cantilever beam impact | 23°C | ASTM D4812 | 3200 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 92 | |
| Rockwell hardness | R-Scale | ASTM D785 | 127 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| transmissivity | 2540 µm | ASTM D1003 | 85.0 | % |
| Refractive index | | ASTM D542 | 1.600 | |
| Haze | 2540 µm | ASTM D1003 | 1.0 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.