PC LEXAN™ HP4-1H111 SABIC INNOVATIVE US
101
- Unit Price:
- $5356 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility
- Application Areas:medicine Medical/nursing supplies medical care
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Specific volume | ASTMD792 | 0.830 | cm³/g | |
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 11 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 10.0 | cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Water absorption rate | 24hr | ASTMD570 | 0.15 | % |
| Equilibrium,23°C | ASTMD570 | 0.35 | % | |
| Equilibrium,100°C | ASTMD570 | 0.58 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 2 | ASTMD638 | 2370 | Mpa | |
| Bending modulus 5 | ISO178 | 2300 | Mpa | |
| Bending strength 5,6 | ISO178 | 90.0 | Mpa | |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 97.0 | Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | ASTMD1044 | 10.0 | mg |
| Tensile modulus | ISO527-2/1 | 2350 | Mpa | |
| Tensile strength 3 | Yield | ASTMD638 | 62.0 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 63.0 | Mpa |
| Tensile strength 3 | Break | ASTMD638 | 68.0 | Mpa |
| Tensile stress | Break | ISO527-2/50 | 70.0 | Mpa |
| Elongation rate 3 | Yield | ASTMD638 | 7.0 | % |
| Tensile strain | Yield | ISO527-2/50 | 6.0 | % |
| Elongation rate 4 | Break | ASTMD638 | 130 | % |
| Tensile strain | Break | ISO527-2/50 | 110 | % |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 2340 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTIElec | UL746 | 130 | °C | |
| Evolution Calendar intelligent importer | UL746 | 130 | °C | |
| RTIStr | UL746 | 130 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 137 | °C |
| Hot deformation temperature 9 | 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 136 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 132 | °C |
| Hot deformation temperature 9 | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 125 | °C |
| Vicat softening temperature | ASTMD152510 | 154 | °C | |
| -- | ISO306/A50 | 153 | °C | |
| -- | ISO306/B50 | 141 | °C | |
| -- | ISO306/B120 | 142 | °C | |
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：-40to95°C | ASTME831 | 6.8E-05 | cm/cm/°C |
| MD：23to80°C | ISO11359-2 | 7E-05 | cm/cm/°C | |
| specific heat | ASTMC351 | 1250 | J/kg/°C | |
| thermal conductivity | ASTMC177 | 0.19 | W/m/K | |
| ISO8302 | 0.20 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the anti leakage trace index | CTI | UL746 | PLC2 | |
| High arc combustion index | HAI | UL746 | PLC1 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC2 | |
| Hot wire ignition | HWI | UL746 | PLC2 | |
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | ASTMD257 | >1.0E+17 | ohms·cm | |
| IEC60093 | >1.0E+15 | ohms·cm | ||
| Dielectric strength | 3.20mm,inAir | ASTMD149 | 15 | KV/mm |
| 3.20mm,in Oil | IEC60243-1 | 17 | KV/mm | |
| Dielectric constant | 50Hz | ASTMD150 | 3.17 | |
| 60Hz | ASTMD150 | 3.17 | ||
| 1MHz | ASTMD150 | 2.96 | ||
| Relative permittivity | 50Hz | IEC60250 | 2.70 | |
| 60Hz | IEC60250 | 2.70 | ||
| 1MHz | IEC60250 | 2.70 | ||
| Dissipation factor | 50Hz | ASTMD150 | 9E-04 | |
| 60Hz | ASTMD150 | 9E-04 | ||
| 1MHz | ASTMD150 | 0.010 | ||
| 50Hz | IEC60250 | 1E-03 | ||
| 60Hz | IEC60250 | 1E-03 | ||
| 1MHz | IEC60250 | 0.010 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Suspended wall beam gap impact strength 7 | -30°C | ISO180/1A | 10 | kJ/m² |
| 23°C | ISO180/1A | 12 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,EnergyatPeakLoad | ASTMD3763 | 63.0 | J |
| Falling hammer impact | 23°C | ASTMD3029 | 169 | J |
| Tensile impact strength 8 | ASTMD1822 | 577 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Sale | ASTMD785 | 70 | |
| R-Sale | ASTMD785 | 118 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ASTMD542 | 1.586 | ||
| transmissivity | 2540µm | ASTMD1003 | 88.0 | % |
| Haze | 2540µm | ASTMD1003 | 1.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| Extreme Oxygen Index | ASTMD2863 | 25 | % | |
| ISO4589-2 | 25 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.