PC Makrolon® 6717 COVESTRO GERMANY

137

Unit Price:$8645 USD/MT

Packaging Specification:: 25 KG/PKG

Supply Quantity:: 10MT

Delivery Terms:: FOB

Port of Loading:: China Main Port

Accepted Payment Methods:: T/T

Shipping:: Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:high viscosity High temperature resistan
Application Areas:Electronic and electrical Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
density	23°C	ISO 1183	1.20	g/cm³
Apparent density 3		ISO 60	0.66	g/cm³
Melt flow rate	300°C/1.2 kg	ISO 1133	3.0	g/10 min
Molten Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	3.00	cm3/10min
Shrinkage rate	Across Flow	ISO 2577	0.60 到 0.80	%
	Shrinkage rate	流量	ISO 2577	0.60 到 0.80	%
		Shrinkage rate	Across Flow : 280°C, 2.00 mm 4	ISO 294-4	0.75	%
		Shrinkage rate	Shrinkage rate	流量 : 2.00 mm 4	ISO 294-4	0.70	%
Water absorption rate	Saturation, 23°C	ISO 62	0.30	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.12	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	23°C	ISO 527-2/1	2400	Mpa
Tensile stress	Yield, 23°C	ISO 527-2/50	67.0	Mpa
Tensile stress	Tensile stress	Break, 23°C	ISO 527-2/50	65.0	Mpa
Tensile strain	Yield, 23°C	ISO 527-2/50	6.4	%
Tensile strain	Tensile strain	Break, 23°C	ISO 527-2/50	110	%
Nominal tensile fracture strain	23°C	ISO 527-2/50	> 50	%
Bending modulus	23°C	ISO 178	2400	Mpa
Bending stress 5	23°C	ISO 178	98.0	Mpa
Bending stress 5	Bending stress 5	3.5% Strain, 23°C	ISO 178	75.0	Mpa
Flexural Strain at Flexural Strength	23°C	ISO 178	7.1	%

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	139	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	127	°C
Glass transition temperature 8		ISO 11357-2	146	°C
Vicat softening temperature	--	ISO 306/B50	146	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	147	°C
Ball Pressure Test	139°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : 23 to 55°C	ISO 11359-2	7.0E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 55°C	ISO 11359-2	7.0E-5	cm/cm/°C
thermal conductivity	23°C	ISO 8302	0.20	W/m/K
RTI Elec	2.0 mm	UL 746	125	°C
RTI Imp	2.0 mm	UL 746	115	°C
RTI	2.0 mm	UL 746	125	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC 60093	1.0E+16	ohms
Volume resistivity	23°C	IEC 60093	1.0E+16	ohms·cm
Dielectric strength	23°C, 1.00 mm	IEC 60243-1	34	KV/mm
Relative permittivity	23°C, 100 Hz	IEC 60250	3.10
Relative permittivity	Relative permittivity	23°C, 1 MHz	IEC 60250	3.00
Dissipation factor	23°C, 100 Hz	IEC 60250	1.0E-3
Dissipation factor	Dissipation factor	23°C, 1 MHz	IEC 60250	9.0E-3
Leakage Trace Index	Solution A	IEC 60112	225	V
Leakage Trace Index	Leakage Trace Index	Solution B	IEC 60112	125	V

film	Test Condition	Test Method	Test Result	Unit
Water vapor permeability	23°C, 85% RH, 100 µm	ISO 15106-1	15	g/m²/24 hr
Carbon Dioxide Permeability	23°C, 25.4 µm	ISO 2556	16900	cm³/m²/bar/24 hr
Gas Permeation	Carbon Dioxide : 100.0 µm	ISO 2556	3800	cm³/m²/bar/24 hr
	Gas Permeation	Nitrogen : 25.4 µm	ISO 2556	510	cm³/m²/bar/24 hr
		Gas Permeation	Nitrogen : 100.0 µm	ISO 2556	120	cm³/m²/bar/24 hr
			Gas Permeation	Oxygen : 25.4 µm	ISO 2556	2760	cm³/m²/bar/24 hr
			Gas Permeation	Gas Permeation	Oxygen : 100.0 µm	ISO 2556	650	cm³/m²/bar/24 hr

injection	Test Result	Unit
Drying Temperature - Dry Air Dryer	120	°C
Drying time - Dry Air Dryer	4.0	hr
Suggested maximum moisture content	< 0.020	%
Suggested injection volume	30 到 70	%
Temperature at the rear of the barrel	250 到 270	°C
Temperature in the middle of the barrel	270 到 290	°C
Temperature at the front of the material cylinder	285 到 305	°C
Spray nozzle temperature	270 到 305	°C
Processing (melt) temperature	280 到 320	°C
Mold temperature	70 到 110	°C
Back pressure	10.0 到 20.0	Mpa
Exhaust hole depth	0.025 到 0.075	mm

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam gap 7	-30°C, Complete Break	ISO 179/1eA	14	kJ/m²
Impact strength of simply supported beam gap 7	Impact strength of simply supported beam gap 7	23°C, Partial Break	ISO 179/1eA	70	kJ/m²
Impact strength of simply supported beam without notch	-60°C	ISO 179/1eU	无断裂
	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Suspended wall beam gap impact strength 7	-30°C, Complete Break	ISO 180/A	15	kJ/m²
Suspended wall beam gap impact strength 7	Suspended wall beam gap impact strength 7	23°C, Partial Break	ISO 180/A	60	kJ/m²
Multi axis Instrumented Impact Energy	-30°C	ISO 6603-2	65.0	J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	60.0	J
Multi axis Instrumented Peak Impact Force	-30°C	ISO 6603-2	6400	N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	5500	N

hardness	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness		ISO 2039-1	115	Mpa

optical performance	Test Condition	Test Method	Test Result	Unit
Refractive index 18		ISO 489	1.586
transmissivity	1000 µm	ISO 13468-2	87.0	%
	transmissivity	2000 µm	ISO 13468-2	86.0	%
		transmissivity	3000 µm	ISO 13468-2	85.0	%
		transmissivity	transmissivity	4000 µm	ISO 13468-2	84.0	%
ISO 9660			ISO 7391-PC,MFLR,(,,)-05-9

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	2.0 mm	UL 94	V-0
Burning wire flammability index	0.75 mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	1.5 mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	Burning wire flammability index	3.0 mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	0.75 mm	IEC 60695-2-13	875	°C
	Hot filament ignition temperature	1.5 mm	IEC 60695-2-13	900	°C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	900	°C
Extreme Oxygen Index 10		ISO 4589-2	43	%
Application of Flame from Small Burner 11		DIN 53438-1, -3	K1, F1
Flash Ignition Temperature		ASTM D1929	450	°C
Needle Flame Test	1.50 mm 12	IEC 60695-11-5	2.0	min
	Needle Flame Test	1.50 mm 13	IEC 60695-11-5	2.0	min
		Needle Flame Test	2.00 mm 12	IEC 60695-11-5	2.0	min
			Needle Flame Test	2.00 mm 13	IEC 60695-11-5	2.0	min
				Needle Flame Test	3.00 mm 13	IEC 60695-11-5	2.0	min
				Needle Flame Test	Needle Flame Test	3.00 mm 12	IEC 60695-11-5	2.0	min
Self Ignition Temperature		ASTM D1929	510	°C
Vertical Bunsen Burner Test	1.00 mm 14	FAR 25.853(b)	passed
	Vertical Bunsen Burner Test	1.00 mm 15	FAR 25.853(a)	passed
		Vertical Bunsen Burner Test	3.00 mm 14	FAR 25.853(b)	passed
		Vertical Bunsen Burner Test	Vertical Bunsen Burner Test	3.00 mm 15	FAR 25.853(a)	passed
Burning rate	> 1.00 mm	ISO 3795	passed
Smoke density	with flame, CO 17	AITM 3.0005	200	ppm
	Smoke density	with flame, Ds 4 min	ASTM E662	< 200
		Smoke density	with flame, HCL 17	AITM 3.0005	< 1.0	ppm
			Smoke density	with flame, HCN 17	AITM 3.0005	notdetectable	ppm
				Smoke density	with flame, HF 17	AITM 3.0005	< 5.0	ppm
					Smoke density	with flame, NO-NO2 17	AITM 3.0005	< 5.0	ppm
					Smoke density	Smoke density	with flame, SO2-H2O 17	AITM 3.0005	< 20	ppm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.