PC TARFLON™ GZ-2510 IDEMITSU JAPAN
161
Unit Price:$3734 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Bromine free Flame retardant Glass fiber reinforced ma Filler: Glass fiber reinf 10% filler by weight 10% filler by weight Phosphorus content Low (to none) Bromine free Flame retardant performan
- Application Areas:LCD application Fitness equipment Industrial applications Printing machine parts
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | ISO 1183 | 1.27 | g/cm³ | |
| Shrinkage rate | TD | Internal Method | 0.6 | % |
| MD: 2.00 mm | Internal Method | 0.4 | % | |
| Water absorption rate | Equilibrium, 23℃, 50% RH | ISO 62 | 0.15 | % |
| Density/specific gravity | ISO1183 | 1.27 | g/cm³ | |
| SpiralFlow2.3 | 内部方法 | 21.0 | CM | |
| Shrinkage rate | TD:2.00mm | 内部方法 | 0.60 | % |
| MD:2.00mm | 内部方法 | 0.40 | % | |
| Water absorption rate 4 | Equilibrium,23°C,50%RH | ISO62 | 0.15 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Yield | ISO527-2 | 80.0 | Mpa |
| Nominal tensile fracture strain | ISO527-2 | 5.0 | % | |
| Bending modulus | ISO178 | 3500 | Mpa | |
| Bending stress | ISO178 | 120 | Mpa | |
| Rockwell hardness | M -Sale | ISO 2039-2 | 65 | |
| Tensile stress | Break | ISO 527-2 | 80 | Mpa |
| Tensile strain | Break | ISO 527-2 | 5 | % |
| Bending modulus | ISO 178 | 3500 | Mpa | |
| bending strength | ISO 178 | 120 | Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 8 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 142 | °C |
| Linear expansion coefficient - flow | ASTM D696 | 0.000045 | cm/cm/℃ | |
| Flame retardant grade | 1.50 mm | UL 94 | V-0 | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 142 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 4.5E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | ASTMD257 | >1.0E+16 | ohms·cm | |
| Dielectric strength | IEC60243-1 | >22 | KV/mm | |
| Dielectric constant | 1MHz | IEC60250 | 2.95 | |
| Dissipation factor | 1MHz | IEC60250 | 9E-03 | |
| Dielectric constant | 1 MHz | IEC 60250 | 2.95 | |
| Arc resistance | ASTM D495 | 110 | sec | |
| Electrical strength | IEC 60243-1 | > 22 | KV/mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179 | 8.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Scale | ISO2039-2 | 65 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Shortcut | >PC-GF10< |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.