PC LEXAN™ 4701-7000 SABIC INNOVATIVE US
95
- Unit Price:
- $5071 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan transparent
- Application Areas:Electronic and electrical
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Molten Volume Flow Rate (MVR) | 300°C/5.0 kg | ISO 1133 | 6.00 | cm3/10min |
| Shrinkage rate - Flow 1 | 内部方法 | 0.90 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2300 | Mpa | |
| Tensile stress | Yield | ISO 527-2/50 | 70.0 | Mpa |
| Tensile strain | Yield | ISO 527-2/50 | 7.0 | % |
| Break | ISO 527-2/50 | > 50 | % | |
| Bending modulus 2 | ISO 178 | 2300 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature 5 | 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Be | 165 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Ae | 150 | °C | |
| Vicat softening temperature | -- | ISO 306/A50 | 185 | °C |
| -- | ISO 306/B50 | 175 | °C | |
| -- | ISO 306/B120 | 170 | °C | |
| Ball Pressure Test | 123 to 127°C | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion - flow | 23 to 80°C | ISO 11359-2 | 8.0E-5 | cm/cm/°C |
| thermal conductivity | ISO 8302 | 0.21 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative permittivity | 1 MHz | IEC 60250 | 3.10 | |
| Dissipation factor | 100 Hz | IEC 60250 | 0.026 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 125 到 135 | °C | ||
| drying time | 3.0 到 4.0 | hr | ||
| Hopper temperature | 60 到 80 | °C | ||
| Temperature at the rear of the barrel | 300 到 320 | °C | ||
| Temperature in the middle of the barrel | 310 到 330 | °C | ||
| Temperature at the front of the material cylinder | 320 到 340 | °C | ||
| Spray nozzle temperature | 320 到 340 | °C | ||
| Processing (melt) temperature | 325 到 360 | °C | ||
| Mold temperature | 100 到 125 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 3 | -30°C | ISO 179/1eA | 13 | kJ/m² |
| 23°C | ISO 179/1eA | 46 | kJ/m² | |
| Simply supported beam without notch impact strength 3 | -30°C | ISO 179/1eU | 无断裂 | |
| 23°C | ISO 179/1eU | 无断裂 | ||
| Suspended wall beam gap impact strength 4 | -30°C | ISO 180/1A | 11 | kJ/m² |
| 23°C | ISO 180/1A | 35 | kJ/m² | |
| Unscented Izod Impact Strength 4 | -30°C | ISO 180/1U | 无断裂 | |
| 23°C | ISO 180/1U | 无断裂 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R -Sale | ISO 2039-2 | 127 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning wire flammability index | 2.0 mm | IEC 60695-2-12 | 850 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.