PC IUPILON™ EFR3000 MITSUBISHI ENGINEERING JAPAN
100
- Unit Price:
- $3905 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility Flame retardant
- Application Areas:Non specific food
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Molding shrinkage rate | ASTM D955 | 0.50-0.70 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.24 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD:3.20mm | 0.50to0.70 | % | |
| MD:3.20mm | 0.50to0.70 | % | ||
| 吸水率(Saturation,23°C) | 0.24 | % | ||
| Melt mass flow rate | 300°C/1.2kg | ISO1133 | 22 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 21.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Nominal tensile fracture strain | ISO527-2 | 67 | % | |
| Bending stress | ISO178 | 92.0 | Mpa | |
| Tensile stress | Yield | ISO527-2 | 61.0 | Mpa |
| Tensile strain | Yield | ISO527-2 | 4.7 | % |
| elongation at break | ASTM D638/ISO 527 | 4.7 | % | |
| Tensile modulus | ASTM D638/ISO 527 | 2300 | kg/cm²(MPa)[Lb/in²] | |
| ISO527-2 | 2300 | Mpa | ||
| tensile strength | ASTM D638/ISO 527 | 61.0 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 2500 | kg/cm²(MPa)[Lb/in²] | |
| ISO178 | 2500 | Mpa | ||
| bending strength | ASTM D790/ISO 178 | 92.0 | kg/cm²(MPa)[Lb/in²] |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | ASTM D648/ISO 75 | 137 | ℃（℉） | |
| 0.45MPa,Unannealed | ISO75-2/B | 137 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 125 | °C | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.000067 | mm/mm.℃ | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 6.6E-05 | cm/cm/°C |
| TD | ISO11359-2 | 6.7E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation factor | 100Hz | IEC60250 | 6E-04 | |
| 1MHz | IEC60250 | 9E-03 | ||
| Dielectric strength | 1.00mm | IEC60243-1 | 31 | KV/mm |
| 3.00mm | IEC60243-1 | 18 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 3.10 | |
| 1MHz | IEC60250 | 3.10 | ||
| Surface resistivity | ASTM D257/IEC 60093 | 6.0E+15 | Ω | |
| IEC60093 | 6E+15 | ohms | ||
| Dielectric constant | ASTM D150/IEC 60250 | 3.10 | ||
| Volume resistivity | ASTM D257/IEC 60093 | 3.0E+16 | Ω.cm | |
| IEC60093 | 3E+16 | ohms·cm | ||
| Dielectric loss | ASTM D150/IEC 60250 | 0.00060 | ||
| ASTM D150/IEC 60250 | 0.0090 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179 | NoBreak |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 1.0mm | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.