PC IUPILON™ GSH2030 9920A BK MITSUBISHI ENGINEERING JAPAN
108
- Unit Price:
- $3570 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20.2MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Filler: Glass fiber reinf 30% filler by weight 30% filler by weight
- Application Areas:fibre
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD:3.20mm | 0.15to0.35 | % | |
| MD:3.20mm | 0.15to0.35 | % | ||
| Water absorption rate | Saturation,23°C | ISO62 | 0.090 | % |
| Melt mass flow rate | 300°C/1.2kg | ISO1133 | 7.0 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 5.20 | cm3/10min |
| Density/specific gravity | ISO1183 | 1.43 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending stress | ISO178 | 126 | Mpa | |
| Tensile stress | Break | ISO527-2 | 75.0 | Mpa |
| Tensile strain | Break | ISO527-2 | 2.5 | % |
| Tensile modulus | ISO527-2 | 6200 | Mpa | |
| Bending modulus | ISO178 | 5800 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 145 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 139 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the anti leakage trace index | CTI | UL746 | PLC4 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179 | 4.0 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 32 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.40mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.