PC LNP™ FARADEX™ DS-1003FRHI BK81715 SABIC INNOVATIVE US
112
- Unit Price:
- $8419 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Non chloro non bromine fl enhance electromagnetic shielding
- Application Areas:Electronic and Electrical Electronic display Industrial applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Across Flow : 24hr | ISO 294-4 | 0.50 | % |
| 流量 : 24hr | ISO 294-4 | 0.40 到 0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Yield | ISO 527-2 | 57.0 | Mpa |
| Break | ISO 527-2 | 55.0 | Mpa | |
| Tensile strain | Yield | ISO 527-2 | 3.8 | % |
| Break | ISO 527-2 | 4.0 到 8.0 | % | |
| Bending stress | ISO 178 | 80.0 | Mpa | |
| Tensile modulus | ISO 527-2/1 | 2800 | Mpa | |
| Bending modulus | ISO 178 | 2600 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature 2 | 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span | ISO 75-2/Bf | 136 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span | ISO 75-2/Af | 125 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ISO 11359-2 | 6.7E-5 | cm/cm/°C |
| Across Flow : -40°C | ISO 11359-2 | 5.6E-5 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shielding effectiveness | 3.00 mm | 内部方法 | 40 到 55 | dB |
| Surface resistivity | ASTM D257 | 1.0E+2 到 1.0E+3 | ohms | |
| Volume resistivity | ASTM D257 | 1.0E+4 | ohms·cm |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 120 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 305 到 325 | °C | ||
| Mold temperature | 95 到 120 | °C | ||
| drying time | 4.0 | hr | ||
| Temperature at the rear of the barrel | 295 到 305 | °C | ||
| Temperature in the middle of the barrel | 310 到 320 | °C | ||
| Temperature at the front of the material cylinder | 320 到 330 | °C | ||
| Back pressure | 0.200 到 0.300 | Mpa | ||
| Screw speed | 30 到 60 | rpm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Non notched cantilever beam impact | 23°C | ASTM D4812 | 1800 | J/m |
| 23°C 2 | ISO 180/1U | 85 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 2.1 mm, Testing by SABIC | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.