PC Makrolon® 6557 010767 COVESTRO GERMANY
128
Unit Price:$3118 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Medium viscosity
- Application Areas:Electrical field Electronic field Industrial applications
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Saturation,23°C | ISO62 | 0.30 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.12 | % | |
| Shrinkage rate | TD | ISO2577 | 0.60to0.80 | % |
| MD | ISO2577 | 0.60to0.80 | % | |
| TD:2.00mm3 | ISO294-4 | 0.70 | % | |
| MD:2.00mm3 | ISO294-4 | 0.65 | % | |
| 熔体质量流动速率 | 300°C/1.2kg | ISO1133 | 10 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 10.0 | cm3/10min |
| Density/specific gravity | 23°C | ISO1183 | 1.20 | g/cm³ |
| Apparent density | ISO60 | 0.64 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Nominal tensile fracture strain | 23°C | ISO527-2/50 | >50 | % |
| Impact strength of simply supported beam gap | -30°C,Complete Break | ISO7391 | 14 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 70 | kJ/m² | |
| Impact strength of simply supported beam without notch | -60°C | ISO179/1eU | NoBreak | |
| -30°C | ISO179/1eU | NoBreak | ||
| 23°C | ISO179/1eU | NoBreak | ||
| Ball pressure hardness | ISO2039-1 | 115 | Mpa | |
| TensileCreepModule | 1hr | ISO899-1 | 2200 | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 1900 | Mpa |
| Tensile stress | Yield,23°C | ISO527-2/50 | 66.0 | Mpa |
| Break,23°C | ISO527-2/50 | 70.0 | Mpa | |
| Tensile strain | Yield,23°C | ISO527-2/50 | 6.1 | % |
| Break,23°C | ISO527-2/50 | 130 | % | |
| Tensile modulus | 23°C | ISO527-2/1 | 2400 | Mpa |
| Suspended wall beam gap impact strength | -30°C,Complete Break | ISO7391 | 12 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 65 | kJ/m² | |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO6603-2 | 6300 | N |
| 23°C | ISO6603-2 | 5400 | N | |
| Multi axis Instrumented Impact Energy | -30°C | ISO6603-2 | 65.0 | J |
| 23°C | ISO6603-2 | 60.0 | J | |
| Bending stress | 3.5%Strain,23°C | ISO178 | 75.0 | Mpa |
| 23°C | ISO178 | 99.0 | Mpa | |
| Bending modulus | 23°C | ISO178 | 2400 | Mpa |
| Bending strain | 23°C | ISO178 | 7.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Glass transition temperature | ISO11357-2 | 144 | °C | |
| Thermal conductivity coefficient | 23°C | ISO8302 | 0.20 | W/m/K |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 136 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 124 | °C | |
| RTIElec | 1.5mm | UL746 | 125 | °C |
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 115 | °C |
| RTIStr | 1.5mm | UL746 | 125 | °C |
| Vicat softening temperature | -- | ISO306/B50 | 143 | °C |
| -- | ISO306/B120 | 144 | °C | |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C | |
| BallPressure Test | 135°C | IEC60695-10-2 | Pass |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative permittivity | 23°C,100Hz | IEC60250 | 3.10 | |
| 23°C,1MHz | IEC60250 | 3.00 | ||
| Leakage Trace Index | SolutionA | IEC60112 | 225 | V |
| SolutionB | IEC60112 | 125 | V | |
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 34 | KV/mm |
| Dissipation factor | 23°C,100Hz | IEC60250 | 8E-04 | |
| 23°C,1MHz | IEC60250 | 9E-03 | ||
| Surface resistivity | IEC60093 | 1E+16 | ohms | |
| Volume resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| WaterVaporTransmission Rate | 23°C,85%RH,100µm | ISO15106-1 | 15 | g/m²/24hr |
| GasPermeation | CarbonDioxide:23°C,25.4µm | ISO2556 | 16900 | cm³/m²/bar/24hr |
| CarbonDioxide:23°C,100.0µm | ISO2556 | 3800 | cm³/m²/bar/24hr | |
| Nitrogen:23°C,25.4µm | ISO2556 | 510 | cm³/m²/bar/24hr | |
| Nitrogen:23°C,100.0µm | ISO2556 | 120 | cm³/m²/bar/24hr | |
| Oxygen:23°C,25.4µm | ISO2556 | 2760 | cm³/m²/bar/24hr | |
| Oxygen:23°C,100.0µm | ISO2556 | 650 | cm³/m²/bar/24hr |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Light transmittance | 1000µm | ISO13468-2 | 89.0 | % |
| 2000µm | ISO13468-2 | 89.0 | % | |
| 3000µm | ISO13468-2 | 88.0 | % | |
| 4000µm | ISO13468-2 | 87.0 | % | |
| Refractive index | ISO489 | 1.586 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm,CL | UL94 | V-2 | |
| 1.5mm | UL94 | V-2 | ||
| 3.0mm | UL94 | V-0 | ||
| Burning wire flammability index | 0.75mm | IEC60695-2-12 | 900 | °C |
| 1.5mm | IEC60695-2-12 | 960 | °C | |
| 3.0mm | IEC60695-2-12 | 960 | °C | |
| Burning rate - US-FMVSS | >1.00mm | ISO3795 | passed | |
| FlashIgnitionTemperature | ASTMD1929 | 460 | °C | |
| GlowWireTest | 1.50mm | EDFHN60E.02 | 750 | °C |
| 3.00mm | EDFHN60E.02 | 750 | °C | |
| Needle flame test | MethodF:1.50mm | IEC60695-11-5 | 2.0 | min |
| MethodF:2.00mm | IEC60695-11-5 | 2.0 | min | |
| MethodF:3.00mm | IEC60695-11-5 | 2.0 | min | |
| MethodK:1.50mm | IEC60695-11-5 | 1.0 | min | |
| MethodK:2.00mm | IEC60695-11-5 | 2.0 | min | |
| MethodK:3.00mm | IEC60695-11-5 | 2.0 | min | |
| Extreme Oxygen Index | ISO4589-2 | 36 | % | |
| SelfIgnition | ASTMD1929 | 530 | °C | |
| ApplicationofFlamefromSmallBurner MethodKandF | 2.00mm | DIN53438-1,-3 | K1,F1 | |
| Hot filament ignition temperature | 0.75mm | IEC60695-2-13 | 875 | °C |
| 1.5mm | IEC60695-2-13 | 875 | °C | |
| 3.0mm | IEC60695-2-13 | 900 | °C |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Shortcut | ISO7391-PC,MFLR,(,,)-09-9 | |||
| ElectrolyticalCorrosion | 23°C | IEC60426 | A1 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.