PC IUPILON™ GPN2020DF-9001 MITSUBISHI THAILAND
110
- Unit Price:
- $2212 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 15MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility enhance Flame retardant Filler: Glass fiber reinf 20% filler by weight
- Application Areas:Fiber grade
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO62 | 0.11 | % |
| Melt flow index | 300℃/1.2Kg | ISO1133 | 13 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 4.0 | kJ/m² |
| elongation at break | 23°C | ISO527-2 | 2.6 | % |
| Tensile modulus | 23°C | ISO527-2 | 6000 | Mpa |
| tensile strength | 23°C | ISO527-2 | 71.0 | Mpa |
| Bending modulus | 23°C | ISO178 | 5800 | Mpa |
| bending strength | 23°C | ISO178 | 128 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPaUnannealed | ISO75-2/Bf | 123 | °C |
| 1.80MPaAnnealed | ISO75-2/Af | 116 | °C | |
| Coefficient of linear expansion | MD | ISO11359-2 | 3.4E-05 | cm/cm/°C |
| TD | ISO11359-2 | 4E-05 | cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.