PC LEXAN™ DMX9455 NA9B049T SABIC INNOVATIVE US
125
- Unit Price:
- $6971 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 74.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:scratch resistance copolymer wear resistant Flame retardant transparent
- Application Areas:Electrical tools Electrical field Electronic field Fitness equipment Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Volume Flow Rate (MVR) 300 ° C/1.2 kg | ISO 1133 | 13 | ||
| Vertical (Flow) | 3.2 mm | Internal | 0.5~0.8 | % |
| abrasion | Internal | 10 | ||
| ASTM D 1044 | 10 | |||
| Water absorption rate | 24 hours | ASTM D570 | 0.08 | % |
| 50% RH, equilib | ASTM D570 | 0.13 | % | |
| equilibrium, 23C | ASTM D570 | 0.28 | % | |
| 23°C/sat | ISO 62 | 0.27 | % | |
| Moisture absorption rate | 23°C / 50% RH | ISO 62 | 0.13 | % |
| 50% RH, 24 hrs | ASTM D 570 | 0.04 | % | |
| Bi Rong | ASTM D792 | 0.85 | ||
| Melt Mass Flow Rate (MFR) 300 ℃/1.2 kg | ASTM D1238 | 14.5 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 50 mm/min | ASTM D638 | 2900 | Mpa |
| 1 mm/min | ISO 527 | 2450 | Mpa | |
| tensile strength | ||||
| Bending modulus | 1.3 mm/min, 50 mm span | ASTM D790 | 2600 | Mpa |
| 2 mm/min | ISO 178 | 2450 | Mpa | |
| Yield (yld) | Type I, 50 mm/min | ASTM D638 | 80 | Mpa |
| 50 mm/min | ISO 527 | 80 | Mpa | |
| Type I, 50 mm/min | ASTM D638 | 7 | % | |
| 50 mm/min | ISO 527 | 7 | % | |
| 1.3 mm/min, 50 mm span | ASTM D790 | 120 | Mpa | |
| 2 mm/min | ISO 178 | 108 | Mpa | |
| Fracture (brk) | Type I, 50 mm/min | ASTM D638 | 70 | % |
| 50 mm/min | ISO 527 | 40 | % | |
| 50 mm/min | ISO 527 | 60 | Mpa | |
| Type I, 50 mm/min | ASTM D638 | 65 | Mpa |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented dart impact energy | ||||
| Total energy at 23 ℃ (73 ℉) | ASTM D3763 | 30 | ||
| Izod Notched -30 ℃ (-22 ℉) | ASTM D256 | 30 | J/m | |
| 80*10*3 | ISO 180/1A | 4 | kJ/m² | |
| Charpy Notched -30 ℃ (-22 ℉) | V-notch Edgew 80*10*3 sp=62mm | ISO 179/1eA | 3 | kJ/m² |
| Charpy Notched at 23 ℃ (73 ℉) | V-notch Edgew 80*10*3 sp=62mm | ISO 179/1eA | 3 | kJ/m² |
| Izod Notched at 23 ℃ (73 ℉) | ASTM D256 | 30 | J/m | |
| 80*10*3 | ISO 180/1A | 5 | kJ/m² | |
| Cantilever beam without notch (Izod Unnotched) 23 ℃ (73 ℉) | ASTM D4812 | NB | J/m | |
| 80*10*3 | ISO 180/1U | NB | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.