PC LEXAN™ HF1140-111 SABIC INNOVATIVE US

Unit Price:
$3312 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
25MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High mobility Good demolding performanc Good forming performance
Application Areas:Safety equipment packing Thin walled products Optical data storage lens container
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Water absorption rate	24 hr	ASTM D570	0.15	%
	Water absorption rate	Equilibrium, 23°C	ASTM D570	0.35	%
	Water absorption rate	Water absorption rate	Equilibrium, 100°C	ASTM D570	0.58	%
Specific volume		ASTM D792	0.830	cm³/g
Melt flow rate	300°C/1.2 kg	ASTM D1238	25	g/10 min
Molten Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	23.0	cm3/10min
Shrinkage rate - flow	3.20 mm	内部方法	0.50 到 0.70	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	10.0	mg
Tensile strength	Yield 3	ASTM D638	62.0	Mpa
	Tensile strength	Yield	ISO 527-2/50	63.0	Mpa
		Tensile strength	Break 3	ASTM D638	65.0	Mpa
		Tensile strength	Tensile strength	Break	ISO 527-2/50	50.0	Mpa
Bending stress	-- 5, 6	ISO 178	90.0	Mpa
Bending stress	Bending stress	Yield, 50.0 mm Span 4	ASTM D790	93.0	Mpa
Tensile modulus	-- 2	ASTM D638	2370	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2350	Mpa
elongation	Yield 3	ASTM D638	6.0	%
	elongation	Yield	ISO 527-2/50	6.0	%
		elongation	Break 3	ASTM D638	120	%
		elongation	elongation	Break	ISO 527-2/50	70	%
Bending modulus	50.0 mm Span 4	ASTM D790	2300	Mpa
Bending modulus	Bending modulus	-- 5	ISO 178	2300	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Vicat softening temperature	--	ISO 306/B50	139	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	140	°C
specific heat		ASTM C351	1250	J/kg/°C
thermal conductivity	--	ASTM C177	0.19	W/m/K
thermal conductivity	thermal conductivity	--	ISO 8302	0.20	W/m/K
RTI		UL 746	130	°C
RTI Imp		UL 746	130	°C
RTI Elec		UL 746	130	°C
Linear coefficient of thermal expansion - flow	-40 to 95°C	ASTM E831	6.8E-5	cm/cm/°C
Linear coefficient of thermal expansion - flow	Linear coefficient of thermal expansion - flow	23 to 80°C	ISO 11359-2	7.0E-5	cm/cm/°C
Thermal deformation temperature under load	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	137	°C
	Thermal deformation temperature under load	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 11	ISO 75-2/Be	133	°C
		Thermal deformation temperature under load	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	126	°C
			Thermal deformation temperature under load	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	126	°C
			Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 11	ISO 75-2/Ae	121	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过

Electrical performance	Test Condition	Test Method	Test Result	Unit
Compared to the Leakage Tracking Index (CTI)		UL 746	PLC 2
Hot wire ignition (HWI)		UL 746	PLC 2
Dielectric strength	3.20 mm, in Air	ASTM D149	15	KV/mm
Dielectric strength	Dielectric strength	3.20 mm, in Oil	IEC 60243-1	17	KV/mm
Dissipation factor	50 Hz	ASTM D150	9.0E-4
	Dissipation factor	60 Hz	ASTM D150	9.0E-4
		Dissipation factor	1 MHz	ASTM D150, IEC 60250	0.010
			Dissipation factor	50 Hz	IEC 60250	1.0E-3
			Dissipation factor	Dissipation factor	60 Hz	IEC 60250	1.0E-3
Surface resistivity		IEC 60093	> 1.0E+15	ohms
Dielectric constant	60 Hz	ASTM D150	3.17
	Dielectric constant	50 kHz	ASTM D150	3.17
		Dielectric constant	1 MHz	ASTM D150	2.96
			Dielectric constant	50 Hz	IEC 60250	2.70
				Dielectric constant	60 Hz	IEC 60250	2.70
				Dielectric constant	Dielectric constant	1 MHz	IEC 60250	2.70
Volume resistivity	--	ASTM D257	> 1.0E+17	ohms·cm
Volume resistivity	Volume resistivity	--	IEC 60093	> 1.0E+15	ohms·cm
High Voltage Arc Traceability Rate (HVTR)		UL 746	PLC 2
High arc combustion index (HAI) 12		UL 746	PLC 1

injection	Test Result	Unit
drying time	3.0 到 4.0	hr
Suggested injection volume	40 到 60	%
Temperature at the rear of the barrel	250 到 270	°C
Temperature in the middle of the barrel	260 到 280	°C
Temperature at the front of the material cylinder	270 到 295	°C
Spray nozzle temperature	265 到 290	°C
Back pressure	0.300 到 0.700	Mpa
Screw speed	40 到 70	rpm
Exhaust hole depth	0.025 到 0.076	mm
drying temperature	120	°C
Suggested maximum moisture content	0.020	%
Processing (melt) temperature	270 到 295	°C
Mold temperature	70 到 95	°C

Impact performance	Test Condition	Test Method	Test Result	Unit
Tensile impact strength 10		ASTM D1822	378	kJ/m²
Non notched cantilever beam impact	23°C	ASTM D4812	3200	J/m
Impact strength of simply supported beam gap 7	-30°C	ISO 179/1eA	10	kJ/m²
Impact strength of simply supported beam gap 7	Impact strength of simply supported beam gap 7	23°C	ISO 179/1eA	12	kJ/m²
Falling hammer impact	23°C	ASTM D3029	169	J
Dart impact equipped with measuring instruments	23°C, Energy at Peak	ASTM D3763	54.0	J

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Scale	ASTM D785	70
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	118

optical performance	Test Condition	Test Method	Test Result	Unit
Refractive index		ASTM D542	1.586
Haze	2540 µm	ASTM D1003	1.0	%
transmissivity	2540 µm	ASTM D1003	88.0	%

flammability	Test Condition	Test Method	Test Result	Unit
Extreme Oxygen Index		ISO 4589-2	25	%
UL flame retardant rating	1.1 mm	UL 94	V-2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.