PC INFINO® HF-1023IM Samsung Cheil South Korea
128
- Unit Price:
- $3119 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance High mobility Impact resistance High liquidity
- Application Areas:Electrical field Electronic field Phone case
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Flow : 3.20 mm | ASTM D955 | 0.44 到 0.53 | % |
| Across Flow : 3.20 mm | ASTM D955 | 0.45 到 0.55 | % | |
| Across Flow : 2.00 mm | ISO 294-4 | 0.45 到 0.55 | % | |
| 流量 : 2.00 mm | ISO 294-4 | 0.44 到 0.53 | % | |
| Water absorption rate | Saturation, 23°C | ASTM D570 | 0.35 | % |
| Melt flow rate | 250°C/10.0 kg | ASTM D1238, ISO 1133 | 22 | g/10 min |
| Density/specific gravity | 本色 | ASTM D792, ISO 1183 | 1.18 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | Yield 3 | ASTM D638 | 59.0 | Mpa |
| Yield | ISO 527-2/50 | 60.0 | Mpa | |
| Break 3 | ASTM D638 | 69.0 | Mpa | |
| Break | ISO 527-2/50 | 96.0 | Mpa | |
| Tensile modulus | -- 3 | ASTM D638 | 1900 | Mpa |
| -- | ISO 527-2/50 | 2100 | Mpa | |
| elongation | Break 3 | ASTM D638 | 120 | % |
| Break | ISO 527-2/50 | 100 | % | |
| Bending modulus | -- 4 | ASTM D790 | 2000 | Mpa |
| -- 5 | ISO 178 | 2100 | Mpa | |
| bending strength | -- 4 | ASTM D790 | 83.0 | Mpa |
| -- 5 | ISO 178 | 88.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed, 4.00 mm | ISO 75-2/B | 133 | °C |
| 0.45 MPa, Annealed, 4.00 mm | ISO 75-2/B | 130 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 126 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm | ISO 75-2/A | 120 | °C | |
| 1.8 MPa, Annealed, 4.00 mm | ISO 75-2/A | 120 | °C | |
| Vicat softening temperature | -- | ISO 306/B50 | 140 | °C |
| -- | ISO 306/B120 | 142 | °C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Temperature at the rear of the barrel | 270 | °C | ||
| Temperature in the middle of the barrel | 280 | °C | ||
| Temperature at the front of the material cylinder | 290 | °C | ||
| Spray nozzle temperature | 300 | °C | ||
| Back pressure | 0.981 到 2.94 | Mpa | ||
| Screw speed | 40 到 80 | rpm | ||
| Injection pressure | 98.1 | Mpa | ||
| Hot air dryer | 2.0 到 4.0 | hr | ||
| 100 | °C | |||
| Vacuum drying machine | 100 | °C | ||
| 4.0 到 6.0 | hr | |||
| Suggested maximum moisture content | < 0.020 | % | ||
| Mold temperature | 80 到 100 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 68 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C, 3.18 mm | ASTM D256 | 690 | J/m |
| 23°C, 6.35 mm | ASTM D256 | 540 | J/m | |
| 23°C 6 | ISO 180/1A | 63 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTM D785 | 120 | |
| R -Sale | ISO 2039-2 | 120 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.