PC LEXAN™ EXL1414B BK1A068 SABIC INNOVATIVE US
124
- Unit Price:
- $3287 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 35MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Processability Moderate liquidity Ductility copolymer Good demolding performanc
- Application Areas:Electrical applications Home appliance components Fitness equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTMD792 | 1.18 | g/cm³ | |
| ISO1183 | 1.19 | g/cm³ | ||
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 10 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 9.00 | cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40to0.80 | % |
| Water absorption rate | 饱和,23°C | ISO62 | 0.35 | % |
| 平衡,23°C,50%RH | ISO62 | 0.15 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ASTMD638 | 2020 | Mpa | |
| ISO527-2/1 | 2150 | Mpa | ||
| Tensile strength | 屈服 | ASTMD638 | 56.0 | Mpa |
| Tensile stress | 屈服 | ISO527-2/50 | 57.0 | Mpa |
| Tensile strength | 断裂 | ASTMD638 | 50.0 | Mpa |
| Tensile stress | 断裂 | ISO527-2/50 | 60.0 | Mpa |
| elongation | 屈服 | ASTMD638 | 6.0 | % |
| Tensile strain | 屈服 | ISO527-2/50 | 6.0 | % |
| elongation | 断裂 | ASTMD638 | 98 | % |
| Tensile strain | 断裂 | ISO527-2/50 | 120 | % |
| Bending modulus | 50.0mm跨距 | ASTMD790 | 2230 | Mpa |
| ISO178 | 2250 | Mpa | ||
| bending strength | ISO178 | 85.0 | Mpa | |
| 屈服,50.0mm跨距 | ASTMD790 | 92.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | -- | ISO306/B50 | 145 | °C |
| -- | ISO306/B120 | 146 | °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7E-05 | cm/cm/°C |
| MD：23到80°C | ISO11359-2 | 7.2E-05 | cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 7E-05 | cm/cm/°C | |
| TD：23to80°C | ISO11359-2 | 7.2E-05 | cm/cm/°C | |
| Hot deformation temperature | 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 140 | °C |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 124 | °C | |
| 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 128 | °C | |
| Vicat softening temperature | ASTMD152510 | 145 | °C | |
| Hot deformation temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 139 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 65 | kJ/m² |
| 23°C | ISO179/1eA | 70 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 770 | J/m |
| 23°C | ASTMD256 | 870 | J/m | |
| -30°C | ISO180/1A | 60 | kJ/m² | |
| 23°C | ISO180/1A | 70 | kJ/m² | |
| Dart impact equipped with measuring instruments | -30°C,TotalEnergy | ASTMD3763 | 77.0 | J |
| 23°C,TotalEnergy | ASTMD3763 | 70.0 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.